Catalytic performance and mechanism of a Pt/TiO2 catalyst for the oxidation of formaldehyde at room temperature
文献类型：期刊论文
| 作者 | Zhang, CB; He, H; Tanaka, K |
| 刊名 | APPLIED CATALYSIS B-ENVIRONMENTAL
 |
| 出版日期 | 2006 |
| 卷号 | 65期号:2015-01-02页码:37-43 |
| 关键词 | formaldehyde noble metal Pt/TiO2 formate species in situ DRIFTS |
| 英文摘要 | The performance of TiO2 supported noble metal (Pt, Rh, Pd and Au) catalysts was examined and compared for the catalytic oxidation of formaldehyde (HCHO). Among them, the Pt/TiO2 was the most active catalyst. The effects of Pt loading and gas hourly space velocity (GHSV) on Pt/TiO2 activity for HCHO oxidation were investigated at a room temperature (20 degrees C). The optimal Pt loading is 1 wt.%. At this loading, HCHO can be completely oxidized to CO2 and H2O over the Pt/TiO2 in a GHSV of 50,000 h(-1) at 20 degrees C. The 1% Pt/TiO2 was characterized using BET, XRD, high resolution (HR) TEM and temperature programmed reduction (TPR) methods. The XRD patterns and HR TEM image show that Pt particles on TiO2 are well dispersed into a size smaller than 1 nm, an important feature for the high activity of the 1% Pt/TiO2. The mechanism of HCHO oxidation was studied with respect to the behavior of adsorbed species on Pt/TiO2 surface at room temperature using in situ DRIFTS. The results indicate that surface formate and CO species are the main reaction intermediates during the HCHO oxidation. The formate species could decompose into adsorbed CO species on the catalyst surface without the presence Of O-2, and the CO was then oxidized to CO, with the presence of O-2. Based on these results, a simplified mechanism for the catalytic oxidation of HCHO over 1% Pt/TiO2 was proposed. (c) 2006 Elsevier B.V. All rights reserved. |
| WOS记录号 | WOS:000237834800005 |
| 源URL | [http://ir.rcees.ac.cn/handle/311016/22839]  |
| 专题 | 生态环境研究中心_环境化学与生态毒理学国家重点实验室 |
| 推荐引用方式 GB/T 7714 | Zhang, CB,He, H,Tanaka, K. Catalytic performance and mechanism of a Pt/TiO2 catalyst for the oxidation of formaldehyde at room temperature[J]. APPLIED CATALYSIS B-ENVIRONMENTAL,2006,65(2015-01-02):37-43. |
| APA | Zhang, CB,He, H,&Tanaka, K.(2006).Catalytic performance and mechanism of a Pt/TiO2 catalyst for the oxidation of formaldehyde at room temperature.APPLIED CATALYSIS B-ENVIRONMENTAL,65(2015-01-02),37-43. |
| MLA | Zhang, CB,et al."Catalytic performance and mechanism of a Pt/TiO2 catalyst for the oxidation of formaldehyde at room temperature".APPLIED CATALYSIS B-ENVIRONMENTAL 65.2015-01-02(2006):37-43. |
入库方式： OAI收割
来源：生态环境研究中心
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。