Bio-inspired laminated graphite nanosheets/copper composites
文献类型：期刊论文
| 作者 | Wang, P; Liu, W; Chen, L; Mu, C; Qi, G; Bian, F |
| 刊名 | RSC ADVANCES
 |
| 出版日期 | 2015 |
| 卷号 | 5期号:63页码:51342—51346 |
| 关键词 | ENHANCED MECHANICAL-PROPERTIES BIOMIMETIC NANOLAMINATED COMPOSITES GRAPHENE-COPPER COMPOSITES FLAKE POWDER-METALLURGY MATRIX COMPOSITES CARBON NANOTUBES LAYER GRAPHENE NANOCOMPOSITES NACRE MICROSTRUCTURE |
| 英文摘要 | As one of the most industrially important metals, copper (Cu) was successfully reinforced with graphite nanosheets (GNSs). A nacre-inspired laminated GNSs/Cu composite material was fabricated by a combination of ball-milling and hot-rolling techniques. During the ball-milling process, the GNSs were in situ produced from graphite exfoliation. The Cu-GNSs composite ingot was hot-rolled into a belt to form a laminated structure. The laminated Cu-GNSs composite material showed improved mechanical properties observed from tensile and three-point bending tests. The Young's modulus of Cu-GNSs composites was up to 170 GPa and the bending strength reached 660 MPa. This processing route was also advantageous in low-cost, mass-producing manufacture. |
| 收录类别 | SCI |
| 语种 | 英语 |
| 公开日期 | 2015-12-24 |
| 源URL | [http://ir.sinap.ac.cn/handle/331007/24403]  |
| 专题 | 上海应用物理研究所_中科院上海应用物理研究所2011-2017年 |
| 推荐引用方式 GB/T 7714 | Wang, P,Liu, W,Chen, L,et al. Bio-inspired laminated graphite nanosheets/copper composites[J]. RSC ADVANCES,2015,5(63):51342—51346. |
| APA | Wang, P,Liu, W,Chen, L,Mu, C,Qi, G,&Bian, F.(2015).Bio-inspired laminated graphite nanosheets/copper composites.RSC ADVANCES,5(63),51342—51346. |
| MLA | Wang, P,et al."Bio-inspired laminated graphite nanosheets/copper composites".RSC ADVANCES 5.63(2015):51342—51346. |
入库方式： OAI收割
来源：上海应用物理研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。