Radiation-induced oxidation of ultra-high molecular weight polyethylene (UHMWPE) powder by gamma rays and electron beams: A clear dependence of dose rate
文献类型：期刊论文
| 作者 | Wang, HL; Xu, L; Hu, JT; Wang, MH; Wu, GZ |
| 刊名 | RADIATION PHYSICS AND CHEMISTRY
 |
| 出版日期 | 2015 |
| 卷号 | 115页码:88—96 |
| 关键词 | OXYGEN-INDUCED RADICALS SURFACE CHARACTERIZATION IRRADIATED POLYETHYLENE MECHANICAL-PROPERTIES CROSS-LINKING ION-BEAMS VITAMIN-E STABILIZATION DEGRADATION ENVIRONMENT |
| ISSN号 | 0969-806X |
| 通讯作者 | Wu, GZ (reprint author), Chinese Acad Sci, Shanghai Inst Appl Phys, Shanghai 201800, Peoples R China. |
| 英文摘要 | Oxidation is an important effect of irradiation on polyethylene in air. In this work, oxidation of ultra-high molecular weight polyethylene (UHMWPE) powder (ca. 110 mu m in diameter) induced by gamma rays (gamma ray) and electron beams (EB) in air resulted in some large differences in properties, such as oxidative scission due to dose rate differences. However, other properties, such as surface wettability and thermal stability were not that greatly affected. The dose-rates used were 0.0019 kGy/s from a cobalt-60 gamma source and 92 kGy/s from an electron beam. The chemical structure, oxidation level, surface wettability and thermal stability of irradiated UHMWPE were analyzed by FT-IR, XPS, TGA and the static contact angle. Hydrophilic carboxyl and carbonyl groups were present on the surface of irradiated UHMWPE after irradiation in air, resulting in a decrease in the contact angle. After irradiation at 300 kGy, the gel content of the gamma ray-irradiated UHMWPE samples decreased to almost zero, while that of EB irradiated UHMWPE decreased to 57%. For UHMWPE powder irradiated by gamma rays at lower doses, radiation-induced oxidation was complete and consistent with a simple theoretic estimation. Surface wettability was primarily affected by surface oxidation, and the oxidation level of UHMWPE could be easily predicted. (C) 2015 Elsevier Ltd. All rights reserved. |
| 语种 | 英语 |
| WOS记录号 | WOS:000359885700015 |
| 公开日期 | 2016-03-08 |
| 源URL | [http://ir.sinap.ac.cn/handle/331007/25025]  |
| 专题 | 上海应用物理研究所_中科院上海应用物理研究所2011-2017年 |
| 推荐引用方式 GB/T 7714 | Wang, HL,Xu, L,Hu, JT,et al. Radiation-induced oxidation of ultra-high molecular weight polyethylene (UHMWPE) powder by gamma rays and electron beams: A clear dependence of dose rate[J]. RADIATION PHYSICS AND CHEMISTRY,2015,115:88—96. |
| APA | Wang, HL,Xu, L,Hu, JT,Wang, MH,&Wu, GZ.(2015).Radiation-induced oxidation of ultra-high molecular weight polyethylene (UHMWPE) powder by gamma rays and electron beams: A clear dependence of dose rate.RADIATION PHYSICS AND CHEMISTRY,115,88—96. |
| MLA | Wang, HL,et al."Radiation-induced oxidation of ultra-high molecular weight polyethylene (UHMWPE) powder by gamma rays and electron beams: A clear dependence of dose rate".RADIATION PHYSICS AND CHEMISTRY 115(2015):88—96. |
入库方式： OAI收割
来源：上海应用物理研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。