Polyamide nanofiltration membrane with high separation performance prepared by EDC/NHS mediated interfacial polymerization
文献类型:期刊论文
作者 | Peng, JM; Su, YL; Chen, WJ; Zhao, XT; Jiang, ZY; Dong, YA; Zhang, Y; Liu, JZ; Cao, XZ; Cao XZ(曹兴忠)![]() |
刊名 | JOURNAL OF MEMBRANE SCIENCE
![]() |
出版日期 | 2013 |
卷号 | 427页码:92-100 |
关键词 | Polyamide composite membrane EDC/NHS activation Nanofiltration High separation properties Structural stability |
英文摘要 | Composite nanofiltration membranes comprising polyamide active layer and polyacrylonitrile (PAN) support were prepared by 1-ethyl-(3-3-dimethylaminopropyl) carbodiimide hydrochloride (EDC)/N-hydroxysuccinimide (NHS) mediated interfacial polymerization. PAN support was first hydrolyzed to create carboxyl groups on surface, which were then activated by EDC/NHS to enhance reactivity with amine groups. Afterwards, activated PAN support was impregnated in aqueous phase containing piperazine (PIP). Finally, PIP impregnated PAN support was immersed in organic phase containing trimesoyl chloride (TMC), where the polyamide active layer was formed on the hydrolyzed PAN support. Fourier Transform Infrared (FT-IR) spectroscopy and X-ray photoelectron spectroscopy (XPS) analysis verified the formation of amide bonds between PIP molecules and carboxyl groups on the hydrolyzed PAN support. Variation energy positron annihilation spectroscopy (VEPAS) measurement manifested that the active layer and interfacial zone of composite membrane became denser owing to EDC/NHS activation. The water flux slightly decreased but the rejection of Orange GII remarkably increased with an increase in EDC concentration. The composite membrane prepared at EDC concentration 100 mM and PIP concentration 0.20 wt% exhibited a flux of MgSO4 solution as high as 511 L/(m(2) h MPa) while the rejection reached 98.5%. The structural stability of the composite membranes after EDC/NHS treatment was greatly enhanced as tested by alcohol treatment. (C) 2012 Elsevier B.V. All rights reserved. |
学科主题 | Engineering; Polymer Science |
收录类别 | SCI |
WOS记录号 | WOS:000311842400010 |
公开日期 | 2016-05-03 |
源URL | [http://ir.ihep.ac.cn/handle/311005/223834] ![]() |
专题 | 中国科学院高能物理研究所 |
推荐引用方式 GB/T 7714 | Peng, JM,Su, YL,Chen, WJ,et al. Polyamide nanofiltration membrane with high separation performance prepared by EDC/NHS mediated interfacial polymerization[J]. JOURNAL OF MEMBRANE SCIENCE,2013,427:92-100. |
APA | Peng, JM.,Su, YL.,Chen, WJ.,Zhao, XT.,Jiang, ZY.,...&曹兴忠.(2013).Polyamide nanofiltration membrane with high separation performance prepared by EDC/NHS mediated interfacial polymerization.JOURNAL OF MEMBRANE SCIENCE,427,92-100. |
MLA | Peng, JM,et al."Polyamide nanofiltration membrane with high separation performance prepared by EDC/NHS mediated interfacial polymerization".JOURNAL OF MEMBRANE SCIENCE 427(2013):92-100. |
入库方式: OAI收割
来源:高能物理研究所
浏览0
下载0
收藏0
其他版本
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。