Preparation and crystallization of nanosized amorphous nickel sulfide by using gamma-irradiation
文献类型：期刊论文
| 作者 | Bian, GZ; Yin, YD; Fu, YL; Wu, ZH; Hu, TD; Liu, T; Wu ZH(吴忠华) ; Hu TD(胡天斗); Liu T(刘涛)
|
| 刊名 | ACTA PHYSICO-CHIMICA SINICA
 |
| 出版日期 | 2000 |
| 卷号 | 16期号:1页码:#REF! |
| 关键词 | gamma-irradiation nanosized amorphous nickel sulfide structure X-ray diffraction EXAFS |
| 其他题名 | γ辐照法制硫化镍纳米非晶及其晶化 |
| 通讯作者 | Bian, GZ (reprint author), Univ Sci & Technol China, Dept Chem Phys, Hefei 230026, Peoples R China. |
| 英文摘要 | Nano-sized amorphous nickel sulfide has been prepared in a mixed aqueous solution of Na2S2O3 and Ni2SO4 compounds using gamma-irradiation at room temperature, The obtained precipitate after gamma-irradiation was washed and dried at 60 degrees C, It was then crystallized by calcination in a flow of argon at 160 - 500 degrees C, respectively, All these samples were characterized by X-ray diffraction and extended X-ray absorption fine structure (EXAFS) spectroscope. No peak is detected in the X-ray diffraction patterns of 60 degrees C dried and 160 degrees C calcined samples, it reveals that particles in these two samples are in amorphous states with high level of disorder, Several weak peaks are found in the pattern of 300 degrees C calcined sample and they become stronger in that of 400 degrees C and 500 degrees C calcined samples. All these peaks are due to NiS compound, EXAFS results demonstrate that the nickel sulfide particles in 60 degrees C dried sample are present in a tetrahetral structure with an average Ni - S coordination distance of 0.221nm and a Ni - S coordination number of 4.4, which are changed to octahedral structures with Ni - S coordination distances of about 0.238nm and Ni - S coordination numbers of near 6.0 after calcined at above 300 degrees C, Both the tetrahedral species and the octahedral species exist in 160 degrees C calcined sample. |
| 学科主题 | Chemistry |
| 类目[WOS] | Chemistry, Physical |
| 收录类别 | SCI |
| WOS记录号 | WOS:000085061800011 |
| 公开日期 | 2016-05-03 |
| 源URL | [http://ir.ihep.ac.cn/handle/311005/225791]  |
| 专题 | 高能物理研究所_多学科研究中心 |
| 推荐引用方式 GB/T 7714 | Bian, GZ,Yin, YD,Fu, YL,et al. Preparation and crystallization of nanosized amorphous nickel sulfide by using gamma-irradiation[J]. ACTA PHYSICO-CHIMICA SINICA,2000,16(1):#REF!. |
| APA | Bian, GZ.,Yin, YD.,Fu, YL.,Wu, ZH.,Hu, TD.,...&刘涛.(2000).Preparation and crystallization of nanosized amorphous nickel sulfide by using gamma-irradiation.ACTA PHYSICO-CHIMICA SINICA,16(1),#REF!. |
| MLA | Bian, GZ,et al."Preparation and crystallization of nanosized amorphous nickel sulfide by using gamma-irradiation".ACTA PHYSICO-CHIMICA SINICA 16.1(2000):#REF!. |
入库方式： OAI收割
来源：高能物理研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。