Microwave sintering carbon nanotube/Ni0.5Zn0.5Fe2O4 composites and their electromagnetic performance
文献类型：期刊论文
| 作者 | Zhou, XB; Shen, L; Li, L; Zhou, SH; Huang, TM; Hu, CF; Pan, WM; Jing, XH; Sun, J; Gao, L |
| 刊名 | JOURNAL OF THE EUROPEAN CERAMIC SOCIETY
 |
| 出版日期 | 2013 |
| 卷号 | 33期号:11页码:2119-2126 |
| 关键词 | Ferrite Carbon nanotube Electromagnetic property Microwave sintering |
| 英文摘要 | Carbon nanotube (CNT)-Ni0.5Zn0.5Fe2O4 powders were prepared by in situ chemical precipitation and hydrothermal processing, and further sintered by microwave sintering technology. The results show that CNTs acted as 'heating source' and promoted the consolidation of composites during the microwave sintering process. However, too much CNTs (such as 5 wt%) led to phase decomposition and reduction of ferrite materials because of the ultra-high localized temperature building up in the interface of CNTs and ferrite grains. The electrical conductivity of composites increased by more than seven orders of magnitude when compared to that of pure Ni0.5Zn0.5Fe2O4, and remained a high value at the temperature of 70K (for example, 1 wt% CNT/Ni0.5Zn0.5Fe2O4 sample kept conductivity of 0.1 S/m). The saturation magnetization was strongly dependent on the mass percentage of CNTs. With the increase in CNT content, both the real and the imaginary permittivity were increased in the frequency region 0.6-5 GHz (L and S bands). According to the measured results of sr and Pr, the frequency-dependent reflectance loss (RL) of CNT/Ni0.5Zn0.5Fe2O4 composite ceramics with different CNT content was evaluated. The CNT-doped ferrite ceramics discussed herein is very promising to be used in an on-beam-line high-order mode (HOM) load in particle accelerators based on superconducting RE due to their excellent low-temperature characteristics. (C) 2013 Elsevier Ltd. All rights reserved. |
| 学科主题 | Materials Science |
| 收录类别 | SCI |
| WOS记录号 | WOS:000319539500008 |
| 公开日期 | 2016-05-03 |
| 源URL | [http://ir.ihep.ac.cn/handle/311005/224190]  |
| 专题 | 中国科学院高能物理研究所 |
| 推荐引用方式 GB/T 7714 | Zhou, XB,Shen, L,Li, L,et al. Microwave sintering carbon nanotube/Ni0.5Zn0.5Fe2O4 composites and their electromagnetic performance[J]. JOURNAL OF THE EUROPEAN CERAMIC SOCIETY,2013,33(11):2119-2126. |
| APA | Zhou, XB.,Shen, L.,Li, L.,Zhou, SH.,Huang, TM.,...&潘卫民.(2013).Microwave sintering carbon nanotube/Ni0.5Zn0.5Fe2O4 composites and their electromagnetic performance.JOURNAL OF THE EUROPEAN CERAMIC SOCIETY,33(11),2119-2126. |
| MLA | Zhou, XB,et al."Microwave sintering carbon nanotube/Ni0.5Zn0.5Fe2O4 composites and their electromagnetic performance".JOURNAL OF THE EUROPEAN CERAMIC SOCIETY 33.11(2013):2119-2126. |
入库方式： OAI收割
来源：高能物理研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。