Mg含量对ADC12铝合金组织及性能的影响
文献类型：期刊论文
| 作者 | 陈名海
|
| 刊名 | 热处理
 |
| 出版日期 | 2011-08-25 |
| 期号 | 4 |
| 关键词 | 镁 ADC12铝合金 显微组织 力学性能 |
| 中文摘要 | 通过加入不同量的镁元素,研究了镁在铝硅铜系ADC12压铸铝合金中的强化作用及强化机制。结果表明,当Mg含量小于1.0%时,ADC12合金的铸态和T6态强度均随Mg含量的增加而提高;而Mg含量高于1.0%时,合金的强度下降。该合金的强化机制主要为形成适量的Mg2Si强化相和细化共晶硅相并不偏聚;过量镁则形成较多的Mg2Si相偏聚于晶界,导致其强度降低。 |
| 英文摘要 | The strengthening of ADC12 Al-Si-Cu series aluminum die-casting alloy resulting from addition of magnesium and its strengthening mechanism were investigated.The results show that the strength of ADC12 alloy in cast or T6 treatment condition increases with the increase of magnesium content that is lower than 1.0%,whereas the strength decreases with the increase of magnesium content that is above 1.0%.The alloy is principally strengthened by formation of suitable amount of Mg2Si phase and refinement of eutectic silicon phase without segregation.Excessive magnesium enable more Mg2Si phase to form and to segregate at grain boundaries,resulting in decrease in strength of the alloy. |
| 语种 | 中文 |
| 公开日期 | 2012-09-17 |
| 源URL | [http://58.210.77.100/handle/332007/770]  |
| 专题 | 苏州纳米技术与纳米仿生研究所_先进材料研究部_李清文团队 |
| 推荐引用方式 GB/T 7714 | 陈名海. Mg含量对ADC12铝合金组织及性能的影响[J]. 热处理,2011(4). |
| APA | 陈名海.(2011).Mg含量对ADC12铝合金组织及性能的影响.热处理(4). |
| MLA | 陈名海."Mg含量对ADC12铝合金组织及性能的影响".热处理 .4(2011). |
入库方式： OAI收割
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。