The interfacial strength and fracture characteristics of ethanol and polymer modified carbon nanotube fibers in their epoxy composites
文献类型：期刊论文
| 作者 | Jingna Zhao（赵静娜） ; Min Li; Min Li; Xiaohua Zhang（张骁骅）; Qingwen Li (李清文)
|
| 刊名 | Carbon
 |
| 出版日期 | 2012 |
| 卷号 | 52期号:16页码:550-558 |
| 通讯作者 | Min Li |
| 英文摘要 | Carbon nanotube (CNT) fibers spun from CNT arrays were used as the reinforcement for epoxy composites, and the interfacial shear strength (IFSS) and fracture behavior were investigated by a single fiber fragmentation test. The IFSS between the CNT fiber and matrix strongly depended on the types of liquid introduced within the fiber. The IFSS of ethanol infiltrated CNT fiber/epoxy varied from 8.32 to 26.64 MPa among different spinning conditions. When long-molecule chain or cross-linked polymers were introduced, besides the increased fiber strength, the adhesion between the polymer modified fiber and the epoxy matrix was also significantly improved. Above all, the IFSS can be up to 120.32 MPa for a polyimide modified CNT fiber, one order of magnitude higher than that of ethanol infiltrated CNT fiber composites, and higher than those of typical carbon fiber/epoxy composites (e.g. 60–90 MPa). Moreover, the composite IFSS is proportional to the tensile strength and modulus of the CNT fiber, and decreases with increasing fiber diameter. The results demonstrate that the interfacial strength of the CNT fiber/epoxy can be significantly tuned by controlling the fiber structure and introducing polymer to optimize the tube–tube interactions within the fiber. |
| 收录类别 | SCI |
| 语种 | 英语 |
| 公开日期 | 2013-01-14 |
| 源URL | [http://58.210.77.100/handle/332007/882]  |
| 专题 | 苏州纳米技术与纳米仿生研究所_先进材料研究部_李清文团队 |
| 通讯作者 | Min Li; Min Li |
| 推荐引用方式 GB/T 7714 | Jingna Zhao,Min Li,Min Li,et al. The interfacial strength and fracture characteristics of ethanol and polymer modified carbon nanotube fibers in their epoxy composites[J]. Carbon,2012,52(16):550-558. |
| APA | Jingna Zhao,Min Li,Min Li,Xiaohua Zhang,&Qingwen Li .(2012).The interfacial strength and fracture characteristics of ethanol and polymer modified carbon nanotube fibers in their epoxy composites.Carbon,52(16),550-558. |
| MLA | Jingna Zhao,et al."The interfacial strength and fracture characteristics of ethanol and polymer modified carbon nanotube fibers in their epoxy composites".Carbon 52.16(2012):550-558. |
入库方式： OAI收割
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。