Fast and one-pot synthesis of silica aerogels via a quasi-solvent-exchange-free ambient pressure drying process
文献类型：期刊论文
| 作者 | Wang, J(王锦); Zhang, YL(张雨露); Wei, Y(危勇); Zhang, XT(张学同)
|
| 刊名 | MICROPOROUS AND MESOPOROUS MATERIALS
 |
| 出版日期 | 2015 |
| 卷号 | 218页码:7 |
| 关键词 | Silica aerogel Solvent-exchange Ambient pressure drying Tetraethoxysilane Condensed silica |
| 通讯作者 | Zhang, XT (张学同) |
| 英文摘要 | A very fast (less than 2 h) and one-pot synthetic strategy was developed for the synthesis of silica aerogels. Organic silica gel was first formed under basic condition by adding a predetermined amount of hexane to a freshly prepared silica sol. After aging at elevated temperature for several minutes, the organogel was mechanically crushed and vigorously stirred in a mixture of trimethylchlorosilane and hexane. Finally, silica aerogel was produced by drying the hydrophobized organogel at temperatures higher than 180 degrees C. The effects of gelation conditions, amount of modification agents, and drying temperatures on the physical properties of the silica aerogels were investigated. The N-2 adsorption and desorption measurements indicated that high BET surface areas (up to 725.8 m(2)/g) could be obtained for the aerogels sintering at 350 degrees C, while that of the silica aerogels dried at 180 degrees C were relative lower (from 379.4 to 564.8 m(2)/g based on the modification conditions). Similar trend was also found in the thermal conductivities of the aerogels, e.g., lower values of thermal conductivity (similar to 0.025 W/mK) were obtained for the sintering samples, while that of the samples without sintering were relative higher (similar to 0.034 W/mK). In summary, a fast ambient pressure drying method has been developed, which show a great potential to synthesize silica aerogels in the industrial scale. (C) 2015 Elsevier Inc. All rights reserved. |
| 收录类别 | SCI |
| 语种 | 英语 |
| 公开日期 | 2016-05-03 |
| 源URL | [http://ir.sinano.ac.cn/handle/332007/3274]  |
| 专题 | 苏州纳米技术与纳米仿生研究所_先进材料研究部_张学同团队 |
| 推荐引用方式 GB/T 7714 | Wang, J,Zhang, YL,Wei, Y,et al. Fast and one-pot synthesis of silica aerogels via a quasi-solvent-exchange-free ambient pressure drying process[J]. MICROPOROUS AND MESOPOROUS MATERIALS,2015,218:7. |
| APA | Wang, J,Zhang, YL,Wei, Y,&Zhang, XT.(2015).Fast and one-pot synthesis of silica aerogels via a quasi-solvent-exchange-free ambient pressure drying process.MICROPOROUS AND MESOPOROUS MATERIALS,218,7. |
| MLA | Wang, J,et al."Fast and one-pot synthesis of silica aerogels via a quasi-solvent-exchange-free ambient pressure drying process".MICROPOROUS AND MESOPOROUS MATERIALS 218(2015):7. |
入库方式： OAI收割
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。