N对TWIP钢马氏体相变及力学性能的影响
文献类型：期刊论文
| 作者 | 黄宝旭1,2; 王长征1; 王晓东3; 戎咏华3 |
| 刊名 | 金属学报
 |
| 出版日期 | 2012 |
| 卷号 | 48期号:7页码:769-774 |
| 关键词 | TWIP钢 马氏体相变 力学性能 TWIP steel martensitic transformation mechanical property |
| ISSN号 | 0412-1961 |
| 中文摘要 | 以传统TWIP钢为对比, 测试了含N TWIP钢的力学性能, 并利用XRD进行物相分析和TEM进行做观结构表征. 结果表明, 在由fcc或hcp结构向bcc结构马氏体进行相变时, 晶体结构中的最大间隙由0.1047 nm降低至0.0725 nm. 间隙原子N的存在显著增大bcc结构的晶格畸变能, 提高α马氏体切变的阻力, 因而强烈抑制α马氏体相变, 导致组织中hcp结构ε相含量大幅度增加, 提高了TWIP钢的强度, 但也降低了钢的塑性. 另外, 奥氏体平均和区域层错几率的计算及微观组织分析结果表明,形变增加层错的数量, 而马氏体相变消耗层错, 从而减少层错数量. |
| 英文摘要 | Twinning induced plasticity (TWIP) steels show large elongation and high tensile strength, exhibiting a super balance between strength and plasticity. Until now, the effects of Mn, Si and Al on stacking fault energy (SFE) and phase transformation of TWIP steel had been investigated, but the effect of N on phase transformation, especially martensite transformation in TWIP steel has not been reported. In the present paper, the mechanical properties of TWIP steel with the addition of N were tested. The phases were analyzed by XRD and the microstructure was characterized by TEM. The average and local probabilities of stacking faults were also calculated by using shifts of X ray peak and electron diffraction spot, respectively. Compared with the conventional TWIP steel, the results showed that at a lower SFE level, when fcc austensite or hcp martensite transformed to bcc martensite, the largest interstice decreased from 0.1047 to 0.0725 nm. The lattice distortion energy of bcc martensite was greatly enlarged by N, which situated in the interstices, leading to the suppression of the bcc martensitic transformation. As a result, the content of hcp martensite increased, causing the increase of strength and decrease of plasticity. Besides, the results also showed that deformation increased stacking faults and hcp or bcc martensitic transformation consumed a large number of stacking faults. |
| 学科主题 | 材料科学与物理化学 |
| 收录类别 | SCI |
| 资助信息 | 国家自然科学基金项目50571060;聊城大学校资助计划项目X071007 |
| 语种 | 中文 |
| WOS记录号 | WOS:000306448200001 |
| 公开日期 | 2016-05-03 |
| 源URL | [http://210.77.64.217/handle/362003/19499]  |
| 专题 | 兰州化学物理研究所_固体润滑国家重点实验室 |
| 作者单位 | 1.聊城大学材料科学与工程学院,聊城大学有色金属研究院 2.中国科学院兰州化学物理研究所固体润滑国家重点实验室 3.上海交通大学材料科学与工程学院 |
| 推荐引用方式 GB/T 7714 | 黄宝旭,王长征,王晓东,等. N对TWIP钢马氏体相变及力学性能的影响[J]. 金属学报,2012,48(7):769-774. |
| APA | 黄宝旭,王长征,王晓东,&戎咏华.(2012).N对TWIP钢马氏体相变及力学性能的影响.金属学报,48(7),769-774. |
| MLA | 黄宝旭,et al."N对TWIP钢马氏体相变及力学性能的影响".金属学报 48.7(2012):769-774. |