Interface Reactions Between Sealing Glass and Metal Interconnect Under Static and Dynamic Heat Treatment Conditions
文献类型：期刊论文
| 作者 | Peng, Lian1; Zhu, Qingshan1; Xie, Zhaohui1; Wang, Ping2 |
| 刊名 | JOURNAL OF FUEL CELL SCIENCE AND TECHNOLOGY
 |
| 出版日期 | 2015-12-01 |
| 卷号 | 12期号:6页码:1 |
| 关键词 | sealing glass interface reactions thermal cycling aging solid oxide fuel cells |
| ISSN号 | 1550-624X |
| 通讯作者 | Zhu, QS (reprint author), Chinese Acad Sci, Inst Proc Engn, State Key Lab Multiphase Complex Syst, Zhong Guan Cun,POB 353, Beijing 100190, Peoples R China. |
| 英文摘要 | Chemical compatibility of sealing glass with metal interconnects is a critical issue for planar solid oxide fuel cell (SOFC). In this paper, interface reactions between a sealing glass and a ferritic metal interconnect (SS410) are tested under three different heat treatment conditions: sealing (static), aging (static), and thermal cycling (dynamic). The results show that the BaCrO4 crystals with two different morphology (round-shaped and needle-shaped) form both at the three-phase boundary (where air, glass, and SS410 meet) and on the surface of the sealing glass under the three conditions. Round-shaped BaCrO4 crystals form with low O-2 concentration and short reaction time. Needle-shaped BaCrO4 crystals form with high O-2 concentration and long reaction time. For the thermal cycling condition, the BaCrO4 formed at early stages causes the delamination of the sealing interface. Then, O-2 diffuses into the interior interface along the delamination path, which results in the formation of BaCrO4 at the interior interface. The delaminationenhanced BaCrO4 formation during thermal cycling will lead to crack along the sealing interface, causing the striking increase of leak rates. |
| WOS标题词 | Science & Technology ; Physical Sciences ; Technology |
| 类目[WOS] | Electrochemistry ; Energy & Fuels |
| 研究领域[WOS] | Electrochemistry ; Energy & Fuels |
| 关键词[WOS] | OXIDE FUEL-CELLS ; OXYGEN ; STABILITY ; COMPATIBILITY ; DIFFUSION |
| 收录类别 | SCI |
| 原文出处 | ASME |
| 语种 | 英语 |
| WOS记录号 | WOS:000370968300010 |
| 源URL | [http://ir.ipe.ac.cn/handle/122111/20649]  |
| 专题 | 过程工程研究所_研究所（批量导入） |
| 作者单位 | 1.Chinese Acad Sci, Inst Proc Engn, State Key Lab Multiphase Complex Syst, Zhong Guan Cun,POB 353, Beijing 100190, Peoples R China 2.MEP Minist Environm Protect, Nucl & Radiat Safety Ctr, Beijing 100082, Peoples R China |
| 推荐引用方式 GB/T 7714 | Peng, Lian,Zhu, Qingshan,Xie, Zhaohui,et al. Interface Reactions Between Sealing Glass and Metal Interconnect Under Static and Dynamic Heat Treatment Conditions[J]. JOURNAL OF FUEL CELL SCIENCE AND TECHNOLOGY,2015,12(6):1. |
| APA | Peng, Lian,Zhu, Qingshan,Xie, Zhaohui,&Wang, Ping.(2015).Interface Reactions Between Sealing Glass and Metal Interconnect Under Static and Dynamic Heat Treatment Conditions.JOURNAL OF FUEL CELL SCIENCE AND TECHNOLOGY,12(6),1. |
| MLA | Peng, Lian,et al."Interface Reactions Between Sealing Glass and Metal Interconnect Under Static and Dynamic Heat Treatment Conditions".JOURNAL OF FUEL CELL SCIENCE AND TECHNOLOGY 12.6(2015):1. |
入库方式： OAI收割
来源：过程工程研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。