Influence of Content and Microstructure of Deposited Carbon on Fluidization Behavior of Iron Powder at Elevated Temperatures
文献类型：期刊论文
| 作者 | Lei, Chao1,2; Zhang, Tao3; Zhang, Jianbo1,2; Fan, Chuanlin1; Zhu, Qingshan1; Li, Hongzhong1 |
| 刊名 | isij international
 |
| 出版日期 | 2014 |
| 卷号 | 54期号:3页码:589-595 |
| 关键词 | fluidized bed defluidization prevention iron powder carbon deposition cohesion force |
| 英文摘要 | carbon was deposited on the surface of an iron powder to study the influence of carbon content and microstructure on defluidization prevention at 823-1 173 k. it was found that at each temperature there existed a minimal carbon content (c-min), below which defluidization occurred and c-min increases with increasing operation temperature. microstructure of the deposited carbon, tailored by adjusting deposition conditions, showed significant influence on defluidization. less carbon would be needed to prevent defluidization under a lower rate of carbon deposition since a more uniformly coating of carbon can be obtainable under such conditions. when the fluidizing gas is nitrogen, defluidization will eventually occur after extended time of fluidization even if the initial carbon content is greater than c-min, due to attrition that causes the decrease of carbon content with increasing time of fluidization. however, when the fluidizing gas is 70% co-30% h-2, defluidization will not occur if the initial carbon content is greater than c-min since the carbon content will increase with increasing time of fluidization due to the further deposition of carbon under the co-h-2 atmosphere. furthermore, a fluidizing phase diagram was established for the carbon-coated iron powder and the mechanism of defluidization prevention was explained using a cohesive force based model. |
| WOS标题词 | science & technology ; technology |
| 类目[WOS] | metallurgy & metallurgical engineering |
| 研究领域[WOS] | metallurgy & metallurgical engineering |
| 关键词[WOS] | fe2o3 particles ; bed reduction ; sticking ; defluidization ; prevention ; mechanism ; ores ; gas ; co |
| 收录类别 | SCI |
| 语种 | 英语 |
| WOS记录号 | WOS:000333509300018 |
| 公开日期 | 2016-05-09 |
| 源URL | [http://cas-ir.dicp.ac.cn/handle/321008/145440]  |
| 专题 | 大连化学物理研究所_中国科学院大连化学物理研究所 |
| 作者单位 | 1.Chinese Acad Sci, State Key Lab Multiphase Complex Syst, Inst Proc Engn, Beijing 100190, Peoples R China 2.Univ Chinese Acad Sci, Beijing 100049, Peoples R China 3.Chinese Acad Sci, Dalian Inst Chem Phys, Dalian Natl Lab Clean Energy, Dalian 116023, Peoples R China |
| 推荐引用方式 GB/T 7714 | Lei, Chao,Zhang, Tao,Zhang, Jianbo,et al. Influence of Content and Microstructure of Deposited Carbon on Fluidization Behavior of Iron Powder at Elevated Temperatures[J]. isij international,2014,54(3):589-595. |
| APA | Lei, Chao,Zhang, Tao,Zhang, Jianbo,Fan, Chuanlin,Zhu, Qingshan,&Li, Hongzhong.(2014).Influence of Content and Microstructure of Deposited Carbon on Fluidization Behavior of Iron Powder at Elevated Temperatures.isij international,54(3),589-595. |
| MLA | Lei, Chao,et al."Influence of Content and Microstructure of Deposited Carbon on Fluidization Behavior of Iron Powder at Elevated Temperatures".isij international 54.3(2014):589-595. |
入库方式： OAI收割
来源：大连化学物理研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。