Preparation and Characterization of Graphene Sheet-Polyimide Nanocomposite Films
文献类型:期刊论文
作者 | Zhang, Li-bin1; Wang, Jin-qing1; Yang, Sheng-rong1; Kong, Xiang-zheng2 |
刊名 | acta polymerica sinica |
出版日期 | 2014-11-20 |
期号 | 11页码:1472-1478 |
关键词 | Graphene sheet-polyimide films In situ reduction Anti-static film Surface resistivity Mechanical properties |
英文摘要 | graphene oxide (go) sheets were first synthesized through oxidation of natural graphite by a modified hummers method, and then their homogeneous and stable dispersion in n, n'-dimethylformamide (dmf) was obtained. stable and homogeneous solution mixtures of go and paa (polyamic acid) in dmf at different mass ratios of go/paa were readily prepared. uniform composite films of go-faa were subsequently prepared by solution casting. faa was turned to polyimides (pt) and go reduced in situ to grapheme (gs) at the same time by a subsequent thermal imidization of go-faa films, leading to composite films of gs-pi. electrical resistivity, thermal stability and mechanical property of gs-pi films were studied. the results indicate that the surface resistivity of gs-pi films was significantly decreased with the increase in gs content,lowered to about 10(6) omega, the standard of the anti-static electricity film, in the film prepared with 1.0 wt% of go in go-paa. the tensile strength and the elongation at break of gs-pi composite films were both increased with increase in gs content, reached their maxima in the film prepared with 0.6 wt% of go in go-paa, followed by regular decreases with further increase in gs. different from the tensile strength and the elongation at break, the tensile modulus of gs-pi was in constant increase with gs content in the film. an increase of 37% was detected in gs-pi film prepared with 3.0 wt% of go. moreover, the ductility and the thermal stability of gs-pi were well kept in all the composite films regardless of its gs content. |
WOS标题词 | science & technology ; physical sciences |
类目[WOS] | polymer science |
研究领域[WOS] | polymer science |
关键词[WOS] | polymer nanocomposites ; mechanical-properties ; oxide nanocomposites ; graphite oxide ; composites ; interface ; membrane ; dynamics |
收录类别 | SCI |
语种 | 英语 |
WOS记录号 | WOS:000346552800006 |
公开日期 | 2016-05-09 |
源URL | [http://cas-ir.dicp.ac.cn/handle/321008/145831] |
专题 | 大连化学物理研究所_中国科学院大连化学物理研究所 |
作者单位 | 1.Chinese Acad Sci, Inst Chem Phys, Lanzhou 730000, Peoples R China 2.Univ Jinan, Coll Chem & Chem Engn, Jinan 250022, Peoples R China |
推荐引用方式 GB/T 7714 | Zhang, Li-bin,Wang, Jin-qing,Yang, Sheng-rong,et al. Preparation and Characterization of Graphene Sheet-Polyimide Nanocomposite Films[J]. acta polymerica sinica,2014(11):1472-1478. |
APA | Zhang, Li-bin,Wang, Jin-qing,Yang, Sheng-rong,&Kong, Xiang-zheng.(2014).Preparation and Characterization of Graphene Sheet-Polyimide Nanocomposite Films.acta polymerica sinica(11),1472-1478. |
MLA | Zhang, Li-bin,et al."Preparation and Characterization of Graphene Sheet-Polyimide Nanocomposite Films".acta polymerica sinica .11(2014):1472-1478. |
入库方式: OAI收割
来源:大连化学物理研究所
浏览0
下载0
收藏0
其他版本
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。