Photoluminescence Properties of Efficient Blue-Emitting Phosphor alpha-Ca1.65Sr0.35SiO4:Ce3+: Color Tuning via the Substitutions of Si by Al/Ga/B
文献类型：期刊论文
| 作者 | Li,Kai; Shang,Mengmeng; Lian,Hongzhou; Lin,Jun |
| 刊名 | inorganic chemistry
 |
| 出版日期 | 2015 |
| 卷号 | 54期号:16页码:7992-8002 |
| 关键词 | ENERGY-TRANSFER PROPERTIES SOLID-STATE REACTION RARE-EARTH IONS LUMINESCENCE PROPERTIES WHITE-LIGHT TUNABLE LUMINESCENCE OXYNITRIDE PHOSPHORS CRYSTAL-STRUCTURE MN2+ PHOSPHOR LEDS |
| 通讯作者 | lian,hz |
| 英文摘要 | a series of ce3+-doped alpha-ca1.65sr0.35sio4 (csso) phosphors without and with the substitutions of si by al/ga/b were synthesized via the high-temperature solid-state reaction process. x-ray diffraction patterns and rietveld refinements were used to demonstrate the successful incorporations of al/ga/b into csso:ce3+. without al/ga/b, the ce3+ singly doped csso phosphors present intense blue emission, which correspond to the broad emission bands in visible region with the wavelength range from 360 to 580 nm upon 350 nm excitation. the optimal emission intensity occurs in csso:0.05ce(3+) sample with the emission peak wavelength at 436 nm. with the introduction of al/ga/b into the csso:0.05ce(3+), the emission peak shifts from 436 to 457/465/446 nm under 365 nm excitation, respectively. the red shift of ce3+ emission is attributed to the polyhedral distortion of the cations, resulting in the enhancement of crystal field spitting due to the variations of the adjacent (al/ga/b,si)o-4 polyhedron. moreover, the temperature-dependent photoluminescence was determined to be of light impact to csso:ce3+ with the introduction of al/ga/b. this research is useful for enriching the emission colors of ce3+-activated phosphors. |
| 收录类别 | SCI |
| 语种 | 英语 |
| WOS记录号 | WOS:000359824400035 |
| 公开日期 | 2016-05-31 |
| 源URL | [http://ir.ciac.jl.cn/handle/322003/65072]  |
| 专题 | 长春应用化学研究所_长春应用化学研究所知识产出_期刊论文 |
| 推荐引用方式 GB/T 7714 | Li,Kai,Shang,Mengmeng,Lian,Hongzhou,et al. Photoluminescence Properties of Efficient Blue-Emitting Phosphor alpha-Ca1.65Sr0.35SiO4:Ce3+: Color Tuning via the Substitutions of Si by Al/Ga/B[J]. inorganic chemistry,2015,54(16):7992-8002. |
| APA | Li,Kai,Shang,Mengmeng,Lian,Hongzhou,&Lin,Jun.(2015).Photoluminescence Properties of Efficient Blue-Emitting Phosphor alpha-Ca1.65Sr0.35SiO4:Ce3+: Color Tuning via the Substitutions of Si by Al/Ga/B.inorganic chemistry,54(16),7992-8002. |
| MLA | Li,Kai,et al."Photoluminescence Properties of Efficient Blue-Emitting Phosphor alpha-Ca1.65Sr0.35SiO4:Ce3+: Color Tuning via the Substitutions of Si by Al/Ga/B".inorganic chemistry 54.16(2015):7992-8002. |