Hot corrosion behaviour of La-2(Zr0.7Ce0.3)(2)O-7 thermal barrier coating ceramics exposed to molten calcium magnesium aluminosilicate at different temperatures
文献类型：期刊论文
| 作者 | Zhou,Xin; Zou,Binglin; He,Limin; Xu,Zhenhua; Xu,Jiaying; Mu,Rende; Cao,Xueqiang |
| 刊名 | corrosion science
 |
| 出版日期 | 2015 |
| 卷号 | 100期号:11页码:566-578 |
| 关键词 | CYCLING BEHAVIOR GLASSY DEPOSITS CMAS OXIDE MECHANISMS RESISTANT HEXAALUMINATE INFILTRATION DEGRADATION ATTACK |
| 通讯作者 | he,lm |
| 英文摘要 | hot corrosion studies of la-2(zr0.7ce0.3)(2)o-7 (lz7c3) thermal barrier coating (tbc) ceramics by calcium magnesium aluminosilicate (cmas) glass were conducted at temperatures ranging from 1200 to 1300 degrees c. results indicate that cmas rapidly dissolves lz7c3 and precipitates apatite phase based on (la,ca)(4)(la,ce)(6)(sio4)(6)o-2, fluorite zro2 and other crystalline phases. those reaction products tend to form a continuous crystalline layer at the cmas/lz7c3 interface, which can effectively prevent cmas from further penetration. however, the apatite crystals appear to be lao1.5-lean and are exhibiting chemical composition evolution upon annealing. those may compromise the effectiveness of lz7c3 as a cmas resistant tbc in long-term application. (c) 2015 elsevier ltd. all rights reserved. |
| 收录类别 | SCI |
| 语种 | 英语 |
| WOS记录号 | WOS:000363070100053 |
| 公开日期 | 2016-05-31 |
| 源URL | [http://ir.ciac.jl.cn/handle/322003/65148]  |
| 专题 | 长春应用化学研究所_长春应用化学研究所知识产出_期刊论文 |
| 推荐引用方式 GB/T 7714 | Zhou,Xin,Zou,Binglin,He,Limin,et al. Hot corrosion behaviour of La-2(Zr0.7Ce0.3)(2)O-7 thermal barrier coating ceramics exposed to molten calcium magnesium aluminosilicate at different temperatures[J]. corrosion science,2015,100(11):566-578. |
| APA | Zhou,Xin.,Zou,Binglin.,He,Limin.,Xu,Zhenhua.,Xu,Jiaying.,...&Cao,Xueqiang.(2015).Hot corrosion behaviour of La-2(Zr0.7Ce0.3)(2)O-7 thermal barrier coating ceramics exposed to molten calcium magnesium aluminosilicate at different temperatures.corrosion science,100(11),566-578. |
| MLA | Zhou,Xin,et al."Hot corrosion behaviour of La-2(Zr0.7Ce0.3)(2)O-7 thermal barrier coating ceramics exposed to molten calcium magnesium aluminosilicate at different temperatures".corrosion science 100.11(2015):566-578. |
入库方式： OAI收割
来源：长春应用化学研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。