Interplay between the composition of LLDPE/PS blends and their compatibilization with polyethylene-graft-polystyrene in the foaming behaviour
文献类型：期刊论文
| 作者 | Zhang,Guangchun; Wang,Yuanliang; Xing,Haiping; Qiu,Jian; Gong,Jiang; Yao,Kun; Tan,Haiying; Jiang,Zhiwei; Tang,Tao |
| 刊名 | rsc advances
 |
| 出版日期 | 2015 |
| 卷号 | 5期号:34页码:27181-27189 |
| 关键词 | SUPERCRITICAL CARBON-DIOXIDE DENSITY POLYETHYLENE/POLYPROPYLENE BLENDS POLYMER BLENDS BLOCK-COPOLYMERS RHEOLOGICAL PROPERTIES INTERFACIAL BEHAVIOR CELL MORPHOLOGY IMPACT STRENGTH METHACRYLATE) TEMPERATURE |
| 通讯作者 | tang,t |
| 英文摘要 | polyethylene-g-polystyrene (pe-g-ps) copolymers, which were prepared by the combination of the romp and atrp method, were utilized to compatibilize lldpe/ps blends. on one hand, the effect of pe-g-ps on the morphologies of lldpe/ps blends was investigated. on the other hand, the influences of branch length and added amount of pe-g-ps on the cell morphology of foamed lldpe/ps blends with different compositions were studied using supercritical co2 as a physical foaming agent in a batch foaming process. it was found that the presence of pe-g-ps in the lldpe/ps blends showed different influences on the foaming behaviour, strongly depending on the composition of the blends (i.e. the weight ratio of lldpe and ps). how the interplay of compatibilization and composition of the lldpe/ps blends affected the foaming behaviour of the lldpe/ps blends was studied. a reasonable explanation was ascribed to consecutive states of the interfacial region, resulting from different phase structures of the blends. compared to pristine lldpe and ps, the blends with a sea-island phase structure showed the improved foam morphology, but the presence of pe-g-ps did not strongly influence the foaming behaviours of these blends. in contrast, the presence of pe-g-ps dramatically promoted the foaming ability of lldpe/ps blends with a co-continuous phase structure. it was ascribed to the strengthened interfacial adhesion blocking the channel between two components through which co2 was released, and the viscoelasticity of the blends was not the key factor to determine the foaming behaviour under the same foaming conditions in this work. |
| 收录类别 | SCI |
| 语种 | 英语 |
| WOS记录号 | WOS:000351556800096 |
| 公开日期 | 2016-05-31 |
| 源URL | [http://ir.ciac.jl.cn/handle/322003/67826]  |
| 专题 | 长春应用化学研究所_长春应用化学研究所知识产出_期刊论文 |
| 推荐引用方式 GB/T 7714 | Zhang,Guangchun,Wang,Yuanliang,Xing,Haiping,et al. Interplay between the composition of LLDPE/PS blends and their compatibilization with polyethylene-graft-polystyrene in the foaming behaviour[J]. rsc advances,2015,5(34):27181-27189. |
| APA | Zhang,Guangchun.,Wang,Yuanliang.,Xing,Haiping.,Qiu,Jian.,Gong,Jiang.,...&Tang,Tao.(2015).Interplay between the composition of LLDPE/PS blends and their compatibilization with polyethylene-graft-polystyrene in the foaming behaviour.rsc advances,5(34),27181-27189. |
| MLA | Zhang,Guangchun,et al."Interplay between the composition of LLDPE/PS blends and their compatibilization with polyethylene-graft-polystyrene in the foaming behaviour".rsc advances 5.34(2015):27181-27189. |
入库方式： OAI收割
来源：长春应用化学研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。