The difference between synergistic erosion-corrosion and corrosion of mild steel in SiC suspension
文献类型：期刊论文
| 作者 | Zhao, M ; Wang, JD; Chen, DR; Hao, XP; Wang, BY; Hao XP(郝小鹏); Wang BY(王宝义)
|
| 刊名 | JOURNAL OF ALLOYS AND COMPOUNDS
 |
| 出版日期 | 2008 |
| 卷号 | 466期号:1-2页码:421-428 |
| 关键词 | Metals and alloys Vacancy information Oxidation Positron spectroscopies Photoelectron spectroscopies |
| 通讯作者 | [Zhao, Ming ; Wang, Jiadao ; Chen, Darong] Tsinghua Univ, State Key Lab Tribol, Beijing 100084, Peoples R China ; [Hao, Xiaopeng ; Wang, Baoyi] Chinese Acad Sci, Inst High Energy Phys, Beijing 100049, Peoples R China |
| 英文摘要 | The synergistic erosion-corrosion and corrosion characteristics of mild steel were studied by using rotating disk apparatus and immersing in 0.05 wt.% SiC suspension, respectively. The difference between cavitation erosion and corrosion was determined by scanning electron microscope (SEM), positron annihilation lifetime spectra (PALS) and X-ray photoelectron spectroscopy (XPS). It was found that the propagation of cracks in pit area induced by cavitation erosion did not appear in the course of corrosion. The PALS results showed that the size and number of vacancy cluster induced by cavitation erosion was much larger than that induced by corrosion damage. The results of core level band spectra indicated that there were chemical shifts in the case of cavitation erosion and no chemical shifts except 40 min corrosion in immersion process. The results of valence band spectra implied that the oxidation of mild steel induced by cavitation erosion was more than that induced by corrosion damage. (C) 2007 Elsevier B.V. All rights reserved. |
| 学科主题 | Chemistry; Materials Science; Metallurgy & Metallurgical Engineering |
| 类目[WOS] | Chemistry, Physical ; Materials Science, Multidisciplinary ; Metallurgy & Metallurgical Engineering |
| 研究领域[WOS] | Chemistry ; Materials Science ; Metallurgy & Metallurgical Engineering |
| 原文出处 | SCI |
| 语种 | 英语 |
| WOS记录号 | WOS:000260483400075 |
| 源URL | [http://ir.ihep.ac.cn/handle/311005/237411]  |
| 专题 | 高能物理研究所_多学科研究中心 高能物理研究所_实验物理中心 |
| 作者单位 | 中国科学院高能物理研究所 |
| 推荐引用方式 GB/T 7714 | Zhao, M,Wang, JD,Chen, DR,et al. The difference between synergistic erosion-corrosion and corrosion of mild steel in SiC suspension[J]. JOURNAL OF ALLOYS AND COMPOUNDS,2008,466(1-2):421-428. |
| APA | Zhao, M.,Wang, JD.,Chen, DR.,Hao, XP.,Wang, BY.,...&王宝义.(2008).The difference between synergistic erosion-corrosion and corrosion of mild steel in SiC suspension.JOURNAL OF ALLOYS AND COMPOUNDS,466(1-2),421-428. |
| MLA | Zhao, M,et al."The difference between synergistic erosion-corrosion and corrosion of mild steel in SiC suspension".JOURNAL OF ALLOYS AND COMPOUNDS 466.1-2(2008):421-428. |
入库方式： OAI收割
来源：高能物理研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。