Raman characterization of rutile phase transitions under high-pressure and high-temperature
文献类型：期刊论文
| 作者 | Xiao, WS; Hong, Z; Tan, DY; Weng, KN; Li, YC ; Luo, CJ; Jing, L; Xie, HS; Li YC(李延春); Luo CJ(罗崇举)
|
| 刊名 | SPECTROSCOPY AND SPECTRAL ANALYSIS
 |
| 出版日期 | 2007 |
| 卷号 | 27期号:7页码:1340-1343 |
| 关键词 | rutile high-pressure and high-temperature phase transformations Raman spectra baddeleyite phase Pbca phase alpha-PbO2 phase |
| 通讯作者 | Chinese Acad Sci, Guangzhou Inst Geochem, Guangzhou 510640, Peoples R China ; Chinese Acad Sci, Inst High Energy Phys, Beijing 100094, Peoples R China ; Chinese Acad Sci, Inst Geochem, Guiyang 550002, Peoples R China |
| 英文摘要 | The pressure-induced phase transition of rutile-structured TiO2 was investigated by in-situ Raman spectrum method in a laser-heated diamond anvil cell (DAC). The experiment was conducted at 35 GPa under quasihydrostatic conditions using argon as medium. At room temperature, the rutile-type TiO2 begins to transform to baddeleyite-type phase at 13.4 GPa and completes at 21 GPa, and this new high-pressure structure retains up to 35 GPa, the upmost pressure used in this study. At the pressure of 29.4 GPa the sample of baddeleyite-type TiO2 was heated by an YAG laser to about 1000-1500 degrees C, and then the baddeleyite phase transformed to a Pbca phase. The Pbca phase was heated again at 35.0 GPa and it was still stable. The sample then began to be decompressed, and the Pbca phase of TiO2 transformed to baddeleyite structure at 26.3 GPa, which stayed stable to 11.4, GPa. The formation of Pbca phase from baddeleyite phase needs the condition of high temperature, it transforms back to baddeleyite structure completely at pressure of a little below that on its formation, which suggests the boundary of the two phases can be determined at about 28 GPa. At 7.6 GPa, and the Raman spectrum shows the characteristics of the mixture of two phases of baddeleyite-type and alpha-PbO2 -type, which indicates that the baddeleyite phase transforms to alpha-PbO2 phase at about 7 GPa. The alpha-PbO2-type TiO2 is metastable under ambient condition. |
| 学科主题 | Spectroscopy |
| 类目[WOS] | Spectroscopy |
| 研究领域[WOS] | Spectroscopy |
| 原文出处 | SCI |
| 语种 | 英语 |
| WOS记录号 | WOS:000248697600023 |
| 源URL | [http://ir.ihep.ac.cn/handle/311005/239297]  |
| 专题 | 高能物理研究所_多学科研究中心 |
| 作者单位 | 中国科学院高能物理研究所 |
| 推荐引用方式 GB/T 7714 | Xiao, WS,Hong, Z,Tan, DY,et al. Raman characterization of rutile phase transitions under high-pressure and high-temperature[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS,2007,27(7):1340-1343. |
| APA | Xiao, WS.,Hong, Z.,Tan, DY.,Weng, KN.,Li, YC.,...&刘景.(2007).Raman characterization of rutile phase transitions under high-pressure and high-temperature.SPECTROSCOPY AND SPECTRAL ANALYSIS,27(7),1340-1343. |
| MLA | Xiao, WS,et al."Raman characterization of rutile phase transitions under high-pressure and high-temperature".SPECTROSCOPY AND SPECTRAL ANALYSIS 27.7(2007):1340-1343. |
入库方式： OAI收割
来源：高能物理研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。