Structural evolution of melt-drawn transparent high-density polyethylene during heating and annealing: Synchrotron small-angle X-ray scattering study
文献类型：期刊论文
| 作者 | Jiang, ZY; Tang, YJ; Rieger, J; Enderle, HF; Lilge, D; Roth, SV; Gehrke, R; Wu, ZH ; Li, ZH; Li, XH
|
| 刊名 | EUROPEAN POLYMER JOURNAL
 |
| 出版日期 | 2010 |
| 卷号 | 46期号:9页码:1866-1877 |
| 关键词 | SAXS High-density polyethylene Cylindrical structure Transparent |
| 通讯作者 | [Jiang, Zhiyong ; Tang, Yujing ; Men, Yongfeng] CAS, SKLPPC, CIAC, Changchun 130022, Peoples R China ; [Rieger, Jens] BASF SE, D-67056 Ludwigshafen, Germany ; [Enderle, Hans-Friedrich ; Lilge, Dieter] Basell Polyolefine GmbH, R&D, D-65926 Frankfurt, Germany ; [Roth, Stephan V. ; Gehrke, Rainer] HASYLAB DESY, D-22607 Hamburg, Germany ; [Wu, Zhonghua ; Li, Zhihong] CAS, Inst High Energy Phys, BSRF, Beijing 100039, Peoples R China ; [Li, Xiuhong] CAS, Shanghai Inst Appl Phys, SSRF, Shanghai 201800, Peoples R China |
| 英文摘要 | The morphological development of melt-drawn transparent high-density polyethylene during heating was investigated employing in-situ synchrotron small-angle X-ray scattering (SAXS) technique. The results confirm that at lower temperatures only meridional scattering peaks aligned perpendicular to the extensional flow direction can be observed, indicating a highly oriented lamellar crystallite structure; whereas at higher temperatures an equatorial streak additional to the layer-like meridional scattering pattern develops, reflecting the presence of shish-kebab-like objects in the specimen under investigation. Upon heating, the average thickness of the kebab crystals remains essentially unaffected below 110 degrees C, and subsequently the selective melting of the less stable kebabs proceeds yielding thicker layered lamellar crystals. When the temperature is raised to 131 degrees C, the shish-like formation and the thermally stable kebab crystals melt simultaneously. In addition, the microstructure of the melt-drawn specimen subjected to annealing at elevated temperatures was probed at room temperature. As opposed to the SAXS patterns registered at high temperatures, the SAXS diagram measured after annealing shows no equatorial streak, suggesting that the cylindrical structures could be re-formed. This observation can be explained by assuming that the plate-like kebab crystals with their normal parallel to the stretching direction grow and impinge during cooling to room temperature due to secondary crystallization, which can be verified by in-situ SAXS experiments during annealing and subsequent cooling. (C) 2010 Elsevier Ltd. All rights reserved. |
| 学科主题 | Polymer Science |
| 类目[WOS] | Polymer Science |
| 研究领域[WOS] | Polymer Science |
| 原文出处 | SCI |
| 语种 | 英语 |
| WOS记录号 | WOS:000282357000007 |
| 源URL | [http://ir.ihep.ac.cn/handle/311005/239560]  |
| 专题 | 高能物理研究所_多学科研究中心 高能物理研究所_核技术应用研究中心 |
| 作者单位 | 中国科学院高能物理研究所 |
| 推荐引用方式 GB/T 7714 | Jiang, ZY,Tang, YJ,Rieger, J,et al. Structural evolution of melt-drawn transparent high-density polyethylene during heating and annealing: Synchrotron small-angle X-ray scattering study[J]. EUROPEAN POLYMER JOURNAL,2010,46(9):1866-1877. |
| APA | Jiang, ZY.,Tang, YJ.,Rieger, J.,Enderle, HF.,Lilge, D.,...&李志宏.(2010).Structural evolution of melt-drawn transparent high-density polyethylene during heating and annealing: Synchrotron small-angle X-ray scattering study.EUROPEAN POLYMER JOURNAL,46(9),1866-1877. |
| MLA | Jiang, ZY,et al."Structural evolution of melt-drawn transparent high-density polyethylene during heating and annealing: Synchrotron small-angle X-ray scattering study".EUROPEAN POLYMER JOURNAL 46.9(2010):1866-1877. |
入库方式： OAI收割
来源：高能物理研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。