Evolution Mechanisms of Thermal Shock Cracks in Ceramic Sheet
文献类型：期刊论文
| 作者 | Xu XH(许向红) ; Lin ZK; Sheng SL; Yuan WJ
|
| 刊名 | JOURNAL OF APPLIED MECHANICS-TRANSACTIONS OF THE ASME
 |
| 出版日期 | 2016 |
| 卷号 | 83期号:7页码:71001 |
| 通讯作者邮箱 | xxh@lnm.imech.ac.cn |
| 关键词 | ceramic thermal shock heterogeneity crack interaction depth grading |
| ISSN号 | 0021-8936 |
| 产权排序 | [Xu, Xianghong; Lin, Zhongkang; Sheng, Shilong; Yuan, Wenjun] Chinese Acad Sci, Inst Mech, State Key Lab Nonlinear Mech, 15 Beisihuanxi Rd, Beijing 100190, Peoples R China |
| 通讯作者 | Xu, XH (reprint author), Chinese Acad Sci, Inst Mech, State Key Lab Nonlinear Mech, 15 Beisihuanxi Rd, Beijing 100190, Peoples R China. |
| 中文摘要 | Knowledge of crack initiation, propagation, and corresponding thermal shock failure evolution is prerequisite for effective maintenance of civil engineering so as to avoid disaster. Experimental analysis of the cracking in the ceramic sheets subsequent to water quenching has been conducted. Based on statistical mesoscopic damage mechanics, it was revealed that there are four stages in the process of thermal shock evolution of ceramics subjected to water quenching. The multiple cracks interaction mechanism has been analyzed from the viewpoint of the evolution of the elastic strain energy and stress intensity factor. |
| 分类号 | 一类 |
| 类目[WOS] | Mechanics |
| 研究领域[WOS] | Mechanics |
| 关键词[WOS] | ceramic ; thermal shock ; heterogeneity ; crack interaction ; depth grading |
| 收录类别 | SCI ; EI |
| 原文出处 | http://dx.doi.org/10.1115/1.4033175 |
| 语种 | 英语 |
| WOS记录号 | WOS:000378407800001 |
| 源URL | [http://dspace.imech.ac.cn/handle/311007/59541]  |
| 专题 | 力学研究所_非线性力学国家重点实验室 |
| 推荐引用方式 GB/T 7714 | Xu XH,Lin ZK,Sheng SL,et al. Evolution Mechanisms of Thermal Shock Cracks in Ceramic Sheet[J]. JOURNAL OF APPLIED MECHANICS-TRANSACTIONS OF THE ASME,2016,83(7):71001. |
| APA | 许向红,Lin ZK,Sheng SL,&Yuan WJ.(2016).Evolution Mechanisms of Thermal Shock Cracks in Ceramic Sheet.JOURNAL OF APPLIED MECHANICS-TRANSACTIONS OF THE ASME,83(7),71001. |
| MLA | 许向红,et al."Evolution Mechanisms of Thermal Shock Cracks in Ceramic Sheet".JOURNAL OF APPLIED MECHANICS-TRANSACTIONS OF THE ASME 83.7(2016):71001. |
入库方式： OAI收割
来源：力学研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。