Synthesis of PAA-g-PNIPAM well-defined graft polymer by sequential RAFT and SET-LRP and its application in preparing size-controlled super-paramagnetic Fe3O4 nanoparticles as a stabilizer
文献类型：期刊论文
| 作者 | Jiang XY(姜秀玉)1; Zhai SJ(翟素娟)1; Jiang X(江雪)1; Lu GL(陆国林)1; Huang XY(黄晓宇)1 |
| 刊名 | Polymer
 |
| 出版日期 | 2014 |
| 卷号 | 55期号:16页码:3703-3712 |
| 其他题名 | Synthesis of PAA-g-PNIPAM well-defined graft polymer by sequential RAFT and SET-LRP and its application in preparing size-controlled super-paramagnetic Fe3O4 nanoparticles as a stabilizer |
| 通讯作者 | 陆国林 ; 黄晓宇 |
| 英文摘要 | A series of well-defined double hydrophilic graft copolymers, poly(acrylic acid)-g-poly(N-iso-propylacrylamide) (PAA-g-PNIPAM), was employed as a novel water-soluble coating for constructing superparamagnetic iron oxide nanoparticles. The copolymer was synthesized via a three-step procedure: firstly, a well-defined hydrophobic PtBA-based backbone, poly(tert-butyl 2-((2-chloropropanoyloxy)-methyl)acrylate)-co-poly(tert-butyl acrylate), (PtBCPMA(19)-co-PtBA(18)), was prepared through RAFT copolymerization of a new trifunctional acrylic monomer, tert-butyl 2-((2-chloropropanoyloxy)methyl) acrylate and tert-butyl acrylate; secondly, taking this backbone as a macroinitiator to initiate SET-LRP of N-isopropylacrylamide resulted in well-defined (poly(tert-butyl 24(2-chloropropanoyloxy)methyl)acrylate)-co-poly(tert-butyl acrylate))-g-poly(N-isopropylacrylamide) ((PtBCPMA-co-PtBA)-g-PNIPAM) amphiphilic graft copolymers with relatively narrow polydispersities (M-w/M-n <= 1.31); thirdly, handling (PtBCPMA-co-PtBA)-g-PNIPAM in acidic conditions afforded PAA-g-PNIPAM graft copolymers. The resulting PAA-g-PNIPAM copolymers were directly utilized as a polymeric stabilizer in the preparation of superparamagnetic Fe3O4 nanoparticles. The particle size can be readily tuned in the range of 12.1-23.2 nm by varying the amount of PAA-g-PNIPAM copolymer or the length of PNIPAM side chain. Besides, the structure and properties of prepared Fe3O4/polymer nanocomposites were characterized by XRD, FT-IR, TGA, TEM, and magnetic measurement in detail. (C) 2014 Elsevier Ltd. All rights reserved. |
| 学科主题 | 高分子化学 |
| 收录类别 | SCI |
| 原文出处 | http://dx.doi.org/10.1016/j.polymer.2014.05.050 |
| 语种 | 英语 |
| 源URL | [http://ir.sioc.ac.cn/handle/331003/38901]  |
| 专题 | 上海有机化学研究所_高分子材料研究室 |
| 作者单位 | 1.中科院上海有机化学研究所 2.复旦大学 |
| 推荐引用方式 GB/T 7714 | Jiang XY,Zhai SJ,Jiang X,et al. Synthesis of PAA-g-PNIPAM well-defined graft polymer by sequential RAFT and SET-LRP and its application in preparing size-controlled super-paramagnetic Fe3O4 nanoparticles as a stabilizer[J]. Polymer,2014,55(16):3703-3712. |
| APA | 姜秀玉,翟素娟,江雪,陆国林,&黄晓宇.(2014).Synthesis of PAA-g-PNIPAM well-defined graft polymer by sequential RAFT and SET-LRP and its application in preparing size-controlled super-paramagnetic Fe3O4 nanoparticles as a stabilizer.Polymer,55(16),3703-3712. |
| MLA | 姜秀玉,et al."Synthesis of PAA-g-PNIPAM well-defined graft polymer by sequential RAFT and SET-LRP and its application in preparing size-controlled super-paramagnetic Fe3O4 nanoparticles as a stabilizer".Polymer 55.16(2014):3703-3712. |
入库方式： OAI收割
来源：上海有机化学研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。