高激光损伤阈值溶胶-凝胶ZrO2薄膜
文献类型：期刊论文
| ; | |
| 作者 | 李海元 ; 唐永兴 ; 胡丽丽 |
| 刊名 | 稀有金属材料与工程
 |
| 出版日期 | 2008 |
| 卷号 | 37期号:Suppl. 2页码:185 |
| 关键词 | 溶胶-凝胶 sol-gel 激光损伤阈值 laser induced damage threshold 薄膜 thin film ZrO2 ZrO2 ZrOCl2·8H20 ZrOCl2 center dot 8H(2)O |
| ISSN号 | 1002-185X |
| 其他题名 | Study of sol-gel ZrO2 thin film with high laser damage thresholds |
| 中文摘要 | 采用醇热法水解氧氯化锆（ZrOCl2·8H2O）制备ZrO2溶胶，提拉法涂膜。采用粘度、粒度分布、折射率、IR、DSC、AFM等测试手段对溶胶和薄膜性能进行表征。结果表明，ZrO2溶胶颗粒的平均粒径为18．9nm，薄膜经300℃热处理后折射率可高达1．95，膜层表面均匀平整，表面平均粗糙度仅为0．561nm，膜层的激光损伤阈值为14J／cm^2（1064nm，1ns）。; ZrO2 Sol was prepared by controlling hydrolysis ZrOCl2 center dot 8H(2)O in heated alcoholic solution. The thin films were deposited by dip technique. The characterization of ZrO2 Sol was analyzed by viscosity, particle size analyzer, IR, DSC and AFM analysis. The results showed that the average size of sol particles was 18.9 nm; the refractive index of coatings treated at 300 degrees C was 1.95; the morphology of coatings surface was smooth, and its average roughness was only 0.561 nm. The laser induced damage threshold of ZrO2 coating was 14 j/cm(2) (1064 nm, 1 ns). |
| 分类号 | TB43 |
| 语种 | 中文 |
| 公开日期 | 2009-09-18 ; 2010-10-12 |
| 源URL | [http://ir.siom.ac.cn/handle/181231/3198]  |
| 专题 | 上海光学精密机械研究所_高功率激光物理国家实验室 |
| 推荐引用方式 GB/T 7714 | 李海元,唐永兴,胡丽丽. 高激光损伤阈值溶胶-凝胶ZrO2薄膜, Study of sol-gel ZrO2 thin film with high laser damage thresholds[J]. 稀有金属材料与工程,2008,37(Suppl. 2):185, 187. |
| APA | 李海元,唐永兴,&胡丽丽.(2008).高激光损伤阈值溶胶-凝胶ZrO2薄膜.稀有金属材料与工程,37(Suppl. 2),185. |
| MLA | 李海元,et al."高激光损伤阈值溶胶-凝胶ZrO2薄膜".稀有金属材料与工程 37.Suppl. 2(2008):185. |
入库方式： OAI收割
来源：上海光学精密机械研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。