磷酸盐钕玻璃表面/亚表面损伤特性实验研究
文献类型：期刊论文
| ; | |
| 作者 | 张伟 ; 朱健强 |
| 刊名 | 光学学报
 |
| 出版日期 | 2008 |
| 卷号 | 28期号:2页码:268 |
| 关键词 | 光学检测 Laser glass 光学加工 Laser induced damage threshold 亚表面损伤 Neodymium doped phosphate glass 激光玻璃 Optical detection 激光损伤阈值 Optical fabrication Subsurface damage |
| ISSN号 | 0253-2239 |
| 其他题名 | Experimental investigation on surface/subsurface damage of Nd-doped phosphate glass |
| 中文摘要 | 系统地研究了光学研磨过程中,磨料粒径、载荷大小以及机床转速对钕玻璃表面及亚表面损伤的影响。结果表明,机床转速和载荷基本不改变材料表面粗糙度,而较大载荷或较低机床转速产生较大的亚表面缺陷,表面粗糙度和亚表面缺陷缺陷深度基本与最大磨料粒径呈正比,载荷增倍使亚表面缺陷与表面粗糙度的常数比值增加0.05。研究结果为钕玻璃加工工艺改进提供了参考依据。; This paper investigated the influence of abrasive size, load and spindle speed in grinding process on surface/subsurface damage of Nd-doped phosphate glass experimentally. Results show that the surface roughness is affected little by spindle speed and load. Subsurface damage is much greater in low spindle speed or heavier load. Both surface roughness and subsurface damage are linear to the maximum nominal abrasive size. When the load is doubled, the ratio of subsurface damage to surface roughness increases by 0.05. All the investigating results provide essential foundation for optimizing fabrication techniques of Nd-doped phosphate glass. |
| 收录类别 | EI |
| 语种 | 中文 |
| 公开日期 | 2009-09-18 |
| 源URL | [http://ir.siom.ac.cn/handle/181231/3244]  |
| 专题 | 上海光学精密机械研究所_高功率激光物理国家实验室 |
| 推荐引用方式 GB/T 7714 | 张伟,朱健强. 磷酸盐钕玻璃表面/亚表面损伤特性实验研究, Experimental investigation on surface/subsurface damage of Nd-doped phosphate glass[J]. 光学学报,2008,28(2):268, 272. |
| APA | 张伟,&朱健强.(2008).磷酸盐钕玻璃表面/亚表面损伤特性实验研究.光学学报,28(2),268. |
| MLA | 张伟,et al."磷酸盐钕玻璃表面/亚表面损伤特性实验研究".光学学报 28.2(2008):268. |
入库方式： OAI收割
来源：上海光学精密机械研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。