Microstructure, optical properties and thermal stability of ZrB2 and Zr-B-N thin films as high-temperature solar selective absorbers
文献类型：期刊论文
| 作者 | Sun, Yaoming1,2; Xiao, Xiudi1 ; Chai, Guanqi1; Xu, Gang1; Xiong, Bin1; Zhang, Shaohong1
|
| 刊名 | materials express
 |
| 出版日期 | 2014-06-01 |
| 卷号 | 4期号:3页码:205-212 |
| 关键词 | Solar Selective Absorbers Sputter ZrB2 film Zr-B-N Film Thermal Stability |
| 英文摘要 | zrb2 and zr b n thin films were deposited by dc magnetron sputtering technique. the microstructure and optical properties of thin films were characterized by x-ray diffraction (xrd), x-ray photoelectron spectroscopy (xps), scanning electron microscopy (sem), transmission electron microscopy (tem), energy dispersive x-ray spectroscopy (eds) and spectrophotometer. thin films with high selectivity (a = 95"26%isrt = 5%) were achieved by optimizing the nitrogen content of absorbing layers and thickness of antireflective layer. thermal stability test illustrated that zr b n thin film with high nitrogen content showed weak thermal stability due to the loose morphology of thin films. thus, thin films with low nitrogen content and suitable thickness of si3n4 layer can exhibit superior solar selectivity (a 91.7%lem- = 4.1%) after annealing at 500 c/60 h in air. the xrd, cross-sectional tem and eds results of films annealed at 500 c/100 h in air demonstrated that the solar selectivity degradation of films was due to the surface oxidation of zrb2 layer. moreover, the solar selectivity was still kept at high level (a = 89.05%lsrt = 10.5%) after treating in neutral salt spray for 24 h. it can be deduced that zrb2 thin film by sputtering is a superior candidate as high-temperature solar selective absorbers. |
| WOS标题词 | science & technology ; technology |
| 类目[WOS] | nanoscience & nanotechnology ; materials science, multidisciplinary |
| 研究领域[WOS] | science & technology - other topics ; materials science |
| 关键词[WOS] | sputter-deposition ; ohmic contacts ; mechanical-properties ; coatings ; composite ; zirconium |
| 收录类别 | SCI |
| 语种 | 英语 |
| WOS记录号 | WOS:000338910400003 |
| 源URL | [http://ir.giec.ac.cn/handle/344007/10732]  |
| 专题 | 中国科学院广州能源研究所 |
| 作者单位 | 1.Chinese Acad Sci, Guangzhou Inst Energy Convers, CAS Key Lab Renewable Energy, Guangzhou 510640, Guangdong, Peoples R China 2.Univ Chinese Acad Sci, Beijing 100049, Peoples R China |
| 推荐引用方式 GB/T 7714 | Sun, Yaoming,Xiao, Xiudi,Chai, Guanqi,et al. Microstructure, optical properties and thermal stability of ZrB2 and Zr-B-N thin films as high-temperature solar selective absorbers[J]. materials express,2014,4(3):205-212. |
| APA | Sun, Yaoming,Xiao, Xiudi,Chai, Guanqi,Xu, Gang,Xiong, Bin,&Zhang, Shaohong.(2014).Microstructure, optical properties and thermal stability of ZrB2 and Zr-B-N thin films as high-temperature solar selective absorbers.materials express,4(3),205-212. |
| MLA | Sun, Yaoming,et al."Microstructure, optical properties and thermal stability of ZrB2 and Zr-B-N thin films as high-temperature solar selective absorbers".materials express 4.3(2014):205-212. |
入库方式： OAI收割
来源：广州能源研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。