Corrosion behaviour of Q23513 carbon steel in sediment water from crude oil
文献类型：期刊论文
| 作者 | Cheng, Qingli1,2; Tao, Bin1; Song, Liying3 ; Zhang, Weihua1; Liu, Xiuyun4; Li, Weihua3; Hou, Baorong3; Liu, Quanzhen1
|
| 刊名 | CORROSION SCIENCE
 |
| 出版日期 | 2016-10-01 |
| 卷号 | 111页码:61-71 |
| 关键词 | Carbon steel Weight loss EIS SEM Pitting corrosion |
| 英文摘要 | The effects of sediment water from crude oil on Q235B carbon steel corrosion were investigated through electrochemical measurements, surface characterization, mass loss, and mass gain techniques for 11 weeks of immersion. Results showed that the steel surfaces were covered by scale deposits consisting mainly of CaCO3. Corrosion pits were initiated under the scale deposits. Moreover, a galvanic corrosion cell was generated under the scale deposits, resulting in localized dissolution. However, the scale deposits blocked the transport of corrosion products into the bulk solution, thereby causing the accumulation of corrosion products under the scale deposits. (C) 2016 Elsevier Ltd. All rights reserved. |
| 收录类别 | SCI |
| 语种 | 英语 |
| WOS记录号 | WOS:000382794000006 |
| 版本 | 出版稿 |
| 源URL | [http://ir.qdio.ac.cn/handle/337002/135833]  |
| 专题 | 海洋研究所_海洋腐蚀与防护研究发展中心 |
| 作者单位 | 1.SINOPEC Qingdao Res Inst Safety Engn, 218 Yanan 3th Rd, Qingdao 266700, Shandong, Peoples R China 2.SINOPEC Res Inst Petr Proc, 18 Xueyuan Rd, Beijing, Peoples R China 3.Chinese Acad Sci, Inst Oceanol, Key Lab Marine Environm Corros & Biofouling, Qingdao 266071, Peoples R China 4.Qingdao Univ, Qingdao 266071, Peoples R China |
| 推荐引用方式 GB/T 7714 | Cheng, Qingli,Tao, Bin,Song, Liying,et al. Corrosion behaviour of Q23513 carbon steel in sediment water from crude oil[J]. CORROSION SCIENCE,2016,111:61-71. |
| APA | Cheng, Qingli.,Tao, Bin.,Song, Liying.,Zhang, Weihua.,Liu, Xiuyun.,...&Liu, Quanzhen.(2016).Corrosion behaviour of Q23513 carbon steel in sediment water from crude oil.CORROSION SCIENCE,111,61-71. |
| MLA | Cheng, Qingli,et al."Corrosion behaviour of Q23513 carbon steel in sediment water from crude oil".CORROSION SCIENCE 111(2016):61-71. |
入库方式： OAI收割
来源：海洋研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。