Purpose – The aim of this paper is to study the tribological performance and self-repairing performance of surface-modified nanoscale serpentine powders as lubricant additives in the mineral base oil (5-CST).
Design/methodology/approach – Fourier transform infrared spectroscopy spectra and thermo-gravimetric analysis of both modified and unmodified serpentine were performed to analyse their grafting ratio and suspension after modified using a long-chain naphthene aliphatic acid. The tribological properties of surface-modified serpentine as lubricant additives in 5-CST were evaluated and the worn surfaces were investigated by X-ray photoelectron spectroscopy (XPS) and X-ray absorption near edge structure (XANES).
Findings – The results show that the serpentine particles have high grafting ratio, improving the dispersity in 5-CST. When the serpentine concentration of 1.00 weight per cent is used as additives in 5-CST, friction coefficient reduces by 14.80 per cent under 294 N and wear scar diameter (WSD) decreases by 11.82 per cent. The results of X-ray absorption near edge structure and XANES show that the adsorption and tribochemical reactions occur to form self-repairing lubrication films.
Originality/value – The paper illustrates a tribofilm form on the rubbed surface, which is responsible for the decrease in friction and wear, mainly containing iron oxides, silicon oxides, magnesium oxides and organic compounds. The results are useful for further applications in advanced environmental friendly lubricating oils and additives.