Interlayer design for the graphite-like carbon film with high load-bearing capacity under sliding-friction condition in water
文献类型:期刊论文
作者 | Wang YX(王永欣)1; Pu JB(蒲吉斌)2![]() ![]() ![]() |
刊名 | Applied Surface Science
![]() |
出版日期 | 2014 |
卷号 | 311页码:816-824 |
关键词 | Graphite-like carbon film Interlayer design Load-bearing capacity Sliding-friction Water |
ISSN号 | 0169-4332 |
通讯作者 | 王永欣 |
英文摘要 | GLC films with single Ti interlayer, single Cr interlayer, thickness gradient Cr/C interlayer and composition gradient Cr/C interlayer were fabricated by magnetron sputtering technique. The microstructures, mechanical properties and tribological performance under sliding friction in distilled water and seawater of the as-deposited GLC films were investigated. Results showed that the adhesion strength and the load-bearing capacity under sliding-friction condition in water of GLC film could be improved effectively by interlayer design. GLC film with composition gradient Cr/C interlayer exhibited highest adhesion strength and load-bearing capacity under sliding-friction conditions in water, which was closely related to nano-interlocked microstructure and hard carbide phase formations inside the interlayer. The adhesion strength in scratch test and the critical bearing load under sliding-friction in water of the GLC film with composition gradient Cr/C interlayer exceeded 50 N and 2.73 GPa, respectively. |
学科主题 | 材料科学与物理化学 |
收录类别 | SCI |
资助信息 | the National Natural Science Foundation of China (Grant no. 51202261);the National Basic Research Program of China (973 Program) (Grant no. 2013CB632300) |
语种 | 英语 |
WOS记录号 | WOS:000339037200116 |
源URL | [http://210.77.64.217/handle/362003/20318] ![]() |
专题 | 兰州化学物理研究所_固体润滑国家重点实验室 兰州化学物理研究所_先进润滑与防护材料研究发展中心 |
作者单位 | 1.Chinese Acad Sci, Ningbo Inst Mat Technol & Engn, Key Lab Marine New Mat & Related Technol, Zhejiang Key Lab Marine Mat & Protect Technol, Ningbo 315201, Zhejiang, Peoples R China 2.Chinese Acad Sci, Lanzhou Inst Chem Phys, State Key Lab Solid Lubricat, Lanzhou 730000, Peoples R China 3.Lanzhou Univ Technol, Mat Sci & Engn Coll, Lanzhou 730050, Peoples R China |
推荐引用方式 GB/T 7714 | Wang YX,Pu JB,Wang, Jiafan,et al. Interlayer design for the graphite-like carbon film with high load-bearing capacity under sliding-friction condition in water[J]. Applied Surface Science,2014,311:816-824. |
APA | Wang YX,Pu JB,Wang, Jiafan,Li, Jinlong,Chen JM,&Xue QJ.(2014).Interlayer design for the graphite-like carbon film with high load-bearing capacity under sliding-friction condition in water.Applied Surface Science,311,816-824. |
MLA | Wang YX,et al."Interlayer design for the graphite-like carbon film with high load-bearing capacity under sliding-friction condition in water".Applied Surface Science 311(2014):816-824. |
入库方式: OAI收割
来源:兰州化学物理研究所
浏览0
下载0
收藏0
其他版本
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。