Effects of exposing temperature on corrosion performance of weld joint of a Ni-Mo-Cr alloy
文献类型：期刊论文
| 作者 | Zhu, YS; Hou, J; Yu, GJ; Qiu, J; Chen, SJ; Zhou, XT |
| 刊名 | JOURNAL OF FLUORINE CHEMISTRY
 |
| 出版日期 | 2016 |
| 卷号 | 182期号:-页码:69—75 |
| 关键词 | HYDROCHLORIC-ACID SALT BEHAVIOR INHIBITION FLINAK STEEL |
| ISSN号 | 0022-1139 |
| 通讯作者 | Hou, J ; Zhou, XT (reprint author), Chinese Acad Sci, Shanghai Inst Appl Phys, Shanghai 201800, Peoples R China. |
| 英文摘要 | Corrosion tests of weld joint of a Ni-Mo-Cr alloy were performed in a eutectic LiF-NaF-KF molten salt for 400h at different temperatures (550 degrees C, 700 degrees C, 850 degrees C). Results indicate that the joints exhibit Cr depletion and Fe enrichment in corrosion layer at 700 degrees C and 850 degrees C, that the structural differentiation caused by welding has little impact on the diffusion of the elements in the alloy. The thickness of the Cr depleted layer induced by the corrosion in the molten salt increases with the temperature. The grains of the alloy sample become coarser due to the annealing at higher temperature, which may also enhance the corrosion of the alloy in the salt. (C) 2015 Elsevier B.V. All rights reserved. |
| 收录类别 | SCI |
| 语种 | 英语 |
| WOS记录号 | WOS:000371188600011 |
| 源URL | [http://ir.sinap.ac.cn/handle/331007/25703]  |
| 专题 | 上海应用物理研究所_中科院上海应用物理研究所2011-2017年 |
| 推荐引用方式 GB/T 7714 | Zhu, YS,Hou, J,Yu, GJ,et al. Effects of exposing temperature on corrosion performance of weld joint of a Ni-Mo-Cr alloy[J]. JOURNAL OF FLUORINE CHEMISTRY,2016,182(-):69—75. |
| APA | Zhu, YS,Hou, J,Yu, GJ,Qiu, J,Chen, SJ,&Zhou, XT.(2016).Effects of exposing temperature on corrosion performance of weld joint of a Ni-Mo-Cr alloy.JOURNAL OF FLUORINE CHEMISTRY,182(-),69—75. |
| MLA | Zhu, YS,et al."Effects of exposing temperature on corrosion performance of weld joint of a Ni-Mo-Cr alloy".JOURNAL OF FLUORINE CHEMISTRY 182.-(2016):69—75. |
入库方式： OAI收割
来源：上海应用物理研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。