Joining of silicon carbide ceramic for optical application by reaction bonded technology
文献类型：会议论文
| 作者 | Aifang Zhang; Yichao Chen; Zhiqiang Chen; Hong Liu; Jingzhong Fang |
| 出版日期 | 2010 |
| 会议名称 | Proceedings of the SPIE - The International Society for Optical Engineering |
| 会议日期 | 2010 |
| 卷号 | 7654 |
| 页码 | 765410 (5 pp.) |
| 通讯作者 | Aifang Zhang |
| 中文摘要 | Silicon carbide ceramic is a prospective candidate for the next generation space telescope with a large-scale reflector. In order to reduce the cost of the fabrication of complex shaped component, the joining technology of SiC ceramic is investigated. In this work, SiC ceramic was joined by reaction bonded technology using SiC green preforms successfully. SiC green preforms were fastened together by epoxy resin and joined during the process of one-step Si infiltration. The microstructure and composition of SiC substrate ceramic and the joint is homogeneous and there have no micro-cracks or defects in the joint. The interface reaction layer become smaller and even disappears with carefully surface grinding of the SiC green preforms. The surface roughness of the joined SiC in the area of the joint is 0.95nm rms and there has no significant difference in the surface roughness of the joint area and SiC substrate ceramic. The bending strength of the joined SiC is about 300MPa and the crack occurred inside the SiC substrate but not in the joint. The most important advantage of the method is the joining of SiC ceramics was achieved via one-step Si infiltration process and the joints are homogeneous with the substrate, which is economical and effective. The mechanical and optical properties of the joined SiC can satisfy the requirement of the large-scale telescope in many astronomical instruments. |
| 英文摘要 | Silicon carbide ceramic is a prospective candidate for the next generation space telescope with a large-scale reflector. In order to reduce the cost of the fabrication of complex shaped component, the joining technology of SiC ceramic is investigated. In this work, SiC ceramic was joined by reaction bonded technology using SiC green preforms successfully. SiC green preforms were fastened together by epoxy resin and joined during the process of one-step Si infiltration. The microstructure and composition of SiC substrate ceramic and the joint is homogeneous and there have no micro-cracks or defects in the joint. The interface reaction layer become smaller and even disappears with carefully surface grinding of the SiC green preforms. The surface roughness of the joined SiC in the area of the joint is 0.95nm rms and there has no significant difference in the surface roughness of the joint area and SiC substrate ceramic. The bending strength of the joined SiC is about 300MPa and the crack occurred inside the SiC substrate but not in the joint. The most important advantage of the method is the joining of SiC ceramics was achieved via one-step Si infiltration process and the joints are homogeneous with the substrate, which is economical and effective. The mechanical and optical properties of the joined SiC can satisfy the requirement of the large-scale telescope in many astronomical instruments. |
| 收录类别 | EI ; ISTP |
| 语种 | 英语 |
| 源URL | [http://ir.ioe.ac.cn/handle/181551/7904]  |
| 专题 | 光电技术研究所_轻量化中心 |
| 作者单位 | 中国科学院光电技术研究所 |
| 推荐引用方式 GB/T 7714 | Aifang Zhang,Yichao Chen,Zhiqiang Chen,et al. Joining of silicon carbide ceramic for optical application by reaction bonded technology[C]. 见:Proceedings of the SPIE - The International Society for Optical Engineering. 2010. |
入库方式： OAI收割
来源：光电技术研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。