Structures and Hydrogen Storage Properties of La1-xMgxNi4.25Al0.75 (x=0.0, 0.1, 0.2, 0.3) Alloys
文献类型：期刊论文
| 作者 | Lu, LJ; Cheng, HH; Han, XB; Lei, GH; Tang, XX; Wang, CB; Liu, W; Li, XL |
| 刊名 | RARE METAL MATERIALS AND ENGINEERING
 |
| 出版日期 | 2016 |
| 卷号 | 45期号:1页码:56—61 |
| 关键词 | ELECTROCHEMICAL PROPERTIES LANI4.25AL0.75 MG |
| ISSN号 | 1002-185X |
| 通讯作者 | Cheng, HH (reprint author), Yangzhou Univ, Coll Mech Engn, Yangzhou 225127, Jiangsu, Peoples R China. |
| 英文摘要 | La1-xMgxNi4.25Al0.75 (x=0.0, 0.1, 0.2, 0.3) hydrogen storage alloys were prepared by a three-step induction melting. Their crystal structures and hydrogen storage properties were investigated. Results show that alloys with x=0.0 and 0.1 contain a single LaNi4Al phase; however, those with x=0.2 and 0.3 are composed of LaNi4Al, (La, Mg)Ni-3 and AlNi3 phases. With x increasing from 0.2 to 0.3, the abundances of the secondary phases and the plateau pressures in the pressure-composition isotherms are lifted significantly. Meanwhile, their hydrogen storage capacities are remarkably reduced. It is found that the alloy with x=0.1 possesses the fastest absorption kinetics compared to the others as well as a good hydrogen capacity and a low plateau pressure. |
| 收录类别 | SCI |
| 语种 | 英语 |
| WOS记录号 | WOS:000369551100012 |
| 源URL | [http://ir.sinap.ac.cn/handle/331007/25849]  |
| 专题 | 上海应用物理研究所_中科院上海应用物理研究所2011-2017年 |
| 推荐引用方式 GB/T 7714 | Lu, LJ,Cheng, HH,Han, XB,et al. Structures and Hydrogen Storage Properties of La1-xMgxNi4.25Al0.75 (x=0.0, 0.1, 0.2, 0.3) Alloys[J]. RARE METAL MATERIALS AND ENGINEERING,2016,45(1):56—61. |
| APA | Lu, LJ.,Cheng, HH.,Han, XB.,Lei, GH.,Tang, XX.,...&Li, XL.(2016).Structures and Hydrogen Storage Properties of La1-xMgxNi4.25Al0.75 (x=0.0, 0.1, 0.2, 0.3) Alloys.RARE METAL MATERIALS AND ENGINEERING,45(1),56—61. |
| MLA | Lu, LJ,et al."Structures and Hydrogen Storage Properties of La1-xMgxNi4.25Al0.75 (x=0.0, 0.1, 0.2, 0.3) Alloys".RARE METAL MATERIALS AND ENGINEERING 45.1(2016):56—61. |
入库方式： OAI收割
来源：上海应用物理研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。