The formation of eutectic phases and hot cracks in one Ni-Mo-Cr superalloy
文献类型：期刊论文
| 作者 | Li, J; Shrestha, SL; Long, Y; Li, ZJ; Zhou, XT |
| 刊名 | MATERIALS & DESIGN
 |
| 出版日期 | 2016 |
| 卷号 | 93期号:-页码:324—333 |
| 关键词 | HEAT-AFFECTED ZONE DISCONTINUOUS PRECIPITATION LIQUATION CRACKING INCONEL 718 MICROSTRUCTURE TEMPERATURE ALLOY REACTORS CARBIDE SILICON |
| ISSN号 | 0261-3069 |
| 通讯作者 | Long, Y ; Li, ZJ (reprint author), Chinese Acad Sci, Shanghai Inst Appl Phys, Thorium Molten Salts Reactor Ctr, Shanghai 201800, Peoples R China. |
| 英文摘要 | The structure and the formationmechanism of brittle eutectic phases and hot cracks formed at grain boundaries were investigated in two Ni-Mo-Cr superalloys with different silicon contents (0.06 and 0.46 wt.%). The eutectic phases and hot cracks can be observed along the rolling direction in the 0.46 wt.% Si heat when heated to 1335 degrees C or a higher peak temperature up to 1365 degrees C. Exposure to the higher peak temperatures resulted in the formation of larger eutectic phases and hot cracks in the higher silicon heat. Conversely, there are fewer eutectic phases and smaller hot cracks forming in the low-silicon heat when heated to 1365 degrees C. The eutectic phases were identified as gamma-M6C' type. Based on the constitutional liquation theory and thermodynamic calculations, it was found that the formation of the eutectic phases and hot cracks is due to the localized melting of primary M6C carbides and surrounding Si-riched matrix. The degree of elements segregation in liquid films determines whether liquid films solidify into eutectic phases or cause hot cracks. This model can reasonably explain the observed phenomena and contribute to designing appropriate solid-solution treatment process and welding procedure to avoid brittle phases and cracks in the Ni-Mo-Cr superalloy. (C) 2015 Elsevier Ltd. All rights reserved. |
| 收录类别 | SCI |
| 语种 | 英语 |
| WOS记录号 | WOS:000369587500036 |
| 源URL | [http://ir.sinap.ac.cn/handle/331007/25866]  |
| 专题 | 上海应用物理研究所_中科院上海应用物理研究所2011-2017年 |
| 推荐引用方式 GB/T 7714 | Li, J,Shrestha, SL,Long, Y,et al. The formation of eutectic phases and hot cracks in one Ni-Mo-Cr superalloy[J]. MATERIALS & DESIGN,2016,93(-):324—333. |
| APA | Li, J,Shrestha, SL,Long, Y,Li, ZJ,&Zhou, XT.(2016).The formation of eutectic phases and hot cracks in one Ni-Mo-Cr superalloy.MATERIALS & DESIGN,93(-),324—333. |
| MLA | Li, J,et al."The formation of eutectic phases and hot cracks in one Ni-Mo-Cr superalloy".MATERIALS & DESIGN 93.-(2016):324—333. |
入库方式： OAI收割
来源：上海应用物理研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。