Yb:YAG激光晶体的高温退火和高浓度掺杂效应
文献类型：期刊论文
| 作者 | 邱宏伟; 杨培志; 钟鹤裕; 李红军; 邓佩珍; 徐军; 陈伟 |
| 刊名 | 中国激光
 |
| 出版日期 | 2002 |
| 卷号 | 29期号:5页码:439 |
| 其他题名 | Influence of Annealing and Doping on Yb:YAG |
| 中文摘要 | 测定了提拉法生长的不同掺杂浓度的Yb:YAG晶体从紫外到近红外区的吸收光谱，发现高温氧化气氛退火后原先可见光区色心宽带吸收消失的同时，在紫外区出现新的吸收带，并通过色心的转化对这一现象进行了解释。在紫外区和近红外区吸收光谱中，发现随掺杂浓度的升高220 nm和940 nm附近的吸收带的位置略有移动，提出是由于Yb~(3+)离子掺杂引起的晶格结构畸变导致了Yb:YAG晶体光谱性质的改变。通过X射线衍射对不同掺杂浓度Yb:YAG晶体晶胞参数的测定，证实高的掺杂浓度导致Yb:YAG晶体发生较大的晶格畸变。在不同 |
| 英文摘要 | The UV, visible and IR absorption spectra of annealed and as-grown Yb:YAG grown by Czochralski technique were measured, and some changes of absorption bands and shifts of absorption peaks are observed and discussed. With the disappearance of broad absorption bands of color center at 370 nm and 625 nm, the new absorption band at 254 nm of annealed Yb:YAG is probably the result of change of color center. The little shifts of absorption peaks at 220 nm and 940 nm are regarded as the result of crystal lattice deformation, which was proved by X-ray diffraction. In laser experiment of Yb:YAG crystals, the influence of doping level on laser performance has been observed. |
| 收录类别 | EI |
| 语种 | 中文 |
| 版本 | 出版稿 |
| 源URL | [http://ir.siom.ac.cn/handle/181231/17910]  |
| 专题 | 上海光学精密机械研究所_激光与光电子功能材料研发中心 |
| 作者单位 | 1.邱宏伟, 中国科学院上海光学精密机械研究所, 上海 201800, 中国. 2.杨培志, 中国科学院上海光学精密机械研究所, 上海 201800, 中国. 3.钟鹤裕, 中国科学院上海光学精密机械研究所, 上海 201800, 中国. 4.李红军, 中国科学院上海光学精密机械研究所, 上海 201800, 中国. 5.邓佩珍, 中国科学院上海光学精密机械研究所, 上海 201800, 中国. 6.徐军, 中国科学院上海光学精密机械研究所, 上海 201800, 中国. 7.陈伟, 中国科学院上海光学精密机械研究所, |
| 推荐引用方式 GB/T 7714 | 邱宏伟,杨培志,钟鹤裕,等. Yb:YAG激光晶体的高温退火和高浓度掺杂效应[J]. 中国激光,2002,29(5):439. |
| APA | 邱宏伟.,杨培志.,钟鹤裕.,李红军.,邓佩珍.,...&陈伟.(2002).Yb:YAG激光晶体的高温退火和高浓度掺杂效应.中国激光,29(5),439. |
| MLA | 邱宏伟,et al."Yb:YAG激光晶体的高温退火和高浓度掺杂效应".中国激光 29.5(2002):439. |
入库方式： OAI收割
来源：上海光学精密机械研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。