光学薄膜微缺陷的探测、抑制及其诱导激光损伤机理
文献类型：学位论文
| 作者 | 张东平 |
| 学位类别 | 博士 |
| 答辩日期 | 2005 |
| 授予单位 | 中国科学院上海光学精密机械研究所 |
| 导师 | 邵肄达 ; 范正修 |
| 关键词 | 光学薄膜、激光损伤、损伤阐值、微缺陷、离子后处理、吸收率、表面热透镜技术 |
| 其他题名 | Detection & Suppressing of Micro-defects in Optical Coatings and Laser-induced Damage Mechanism |
| 中文摘要 | 光学薄膜是激光系统中非常重要而又非常脆弱的光学元件，它的损伤问题一直是限制激光系统向高功率、大能量方向发展的主要瓶颈之一。大量的薄膜激光损伤实验表明，薄膜中的微缺陷是导致薄膜激光损伤的重要诱因。微缺陷的控制是其激光损伤闭值提高的一个主要途径。本文将紧紧围绕光学薄膜中与激光损伤密切相关的微缺陷这一中心问题，分别从以下几个方面展开研究. |
| 英文摘要 | The rapid progress in laser systems towards higher output power and both larger and smaller aperture has made the optical components to the limitation. A particularly weak point is optical coatings, which have become a "bottle-neck" problem hampering the further increase of the output, or decrease in the aperture. A lot of experiment results indicate that microdefect is one of the main causes for the films failure, which means if the microdefects are suppressed, the laser-induced damage threshold of the films will be improved. In this dissertation, the microdefects were focused on, and we studied it with the following aspects. |
| 语种 | 中文 |
| 源URL | [http://ir.siom.ac.cn/handle/181231/15809]  |
| 专题 | 上海光学精密机械研究所_学位论文 |
| 推荐引用方式 GB/T 7714 | 张东平. 光学薄膜微缺陷的探测、抑制及其诱导激光损伤机理[D]. 中国科学院上海光学精密机械研究所. 2005. |
入库方式： OAI收割
来源：上海光学精密机械研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。