掺钛蓝宝石晶体热学性质研究
文献类型：期刊论文
| 作者 | 徐民; 司继良; 张小翠; 齐红基; 陈建玉 |
| 刊名 | 人工晶体学报
 |
| 出版日期 | 2014 |
| 卷号 | 43期号:5页码:1043 |
| 关键词 | 掺钛蓝宝石晶体 热膨胀 比热 热扩散率 热导率 |
| 其他题名 | Study on Thermal Properties of Titanium-doped Sapphire Crystal |
| 中文摘要 | 本文系统分析了掺钛蓝宝石晶体的热学性质。在303. 15 ~764.15 K的温度范围内,晶体的主热膨胀系数分别为alpha_1=3.8*l0~(-6) K~(-1)和alpha_3 =6.4x10~(-6) K ~(-1)。298.15 K时,晶体的比热为0. 766 J ? g~(-1) ? K~(-1)。采用激光脉冲法测试了晶体在303 ~570 K温度范围内的热扩散率。掺钛蓝宝石晶体的主热导率分量k与热力学温度T的函数关系通过拟合获得,为k_1=-626. 60772/(-2.52108r + 706.53622) +5.96781和 k_3=-1347.76226/(-2.37632T + 616.40571) +5.88351. |
| 英文摘要 | The thermal properties of titanium-doped sapphire crystal were systematically analyzed. The principal thermal expansion coefficients were measured to be a_1 =3.8 x 10~(-6) K~(-1) and alpha_3 = 6. 4 x 10~(-6) K~(-1) over the temperature range of 303. 15-764. 15 K with a thermal dilatometer. The experimental specific heat was 0. 766 J. g~(-1). K~(-1)at 298. 15 K. The thermal diffusivity of the crystal was measured over the temperature range of 303-570 K for the first time through the laser flash method. Dependences of principal thermal conductivity components k on thermodynamic temperature T were fitted to be k_1 =-626. 60772/(-2. 52108T + 706. 53622) + 5. 96781 and k_3 =-1347.76226/(-2. 37632T + 616. 40571) +5.88351 |
| 收录类别 | CSCD |
| 语种 | 英语 |
| 版本 | 出版稿 |
| 源URL | [http://ir.siom.ac.cn/handle/181231/12860]  |
| 专题 | 上海光学精密机械研究所_中科院强激光材料重点实验室 |
| 作者单位 | 1.徐民, 中国科学院上海光学精密机械研究所强激光材料重点实验室, 上海 201800, 中国. 2.司继良, 中国科学院上海光学精密机械研究所强激光材料重点实验室, 上海 201800, 中国. 3.张小翠, 中国科学院上海光学精密机械研究所强激光材料重点实验室, 上海 201800, 中国. 4.齐红基, 中国科学院上海光学精密机械研究所强激光材料重点实验室, 上海 201800, 中国. 5.陈建玉, 中国科学院上海光学精密机械研究所强激光材料重点实验室, 上海 201800, 中国. |
| 推荐引用方式 GB/T 7714 | 徐民,司继良,张小翠,等. 掺钛蓝宝石晶体热学性质研究[J]. 人工晶体学报,2014,43(5):1043. |
| APA | 徐民,司继良,张小翠,齐红基,&陈建玉.(2014).掺钛蓝宝石晶体热学性质研究.人工晶体学报,43(5),1043. |
| MLA | 徐民,et al."掺钛蓝宝石晶体热学性质研究".人工晶体学报 43.5(2014):1043. |
入库方式： OAI收割
来源：上海光学精密机械研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。