Degradation mechanism of laser-induced damage of porous ZrO2/SiO2 high reflective films in vacuum
文献类型：期刊论文
| 作者 | Ling, Xiulan; Wang, Gao; Liu, Xiaofeng |
| 刊名 | optik
 |
| 出版日期 | 2015 |
| 卷号 | 126期号:19页码:2026 |
| 通讯作者 | ling, xl (reprint author), north univ china, minist educ, key lab instrumentat sci & dynam measurement, taiyuan 030051, peoples r china. |
| 英文摘要 | degradation mechanism of laser-induced damage of porous zro2/sio2 high reflective films was discussed in vacuum. the experimental results show that the laser-induced damage (lidt) in vacuum dropped to 57% of its atmospheric value and 65% of the value filled with air after vacuum pumping for the high reflective films. typical damage micrographs of the films in air and in vacuum were obtained, showing the distinct damage morphologies. such a degradation mechanism of laser-induced damage was found to originate from the water desorption on the surface and internally in porous films, which could cause a decrease of the thermal conductivity. a theoretical and kinetic model was used to illustrate the occurrence of the damage and corresponding damage morphologies. (c) 2015 elsevier gmbh. all rights reserved. |
| 收录类别 | SCI |
| 语种 | 英语 |
| 版本 | 出版稿 |
| 源URL | [http://ir.siom.ac.cn/handle/181231/13829]  |
| 专题 | 上海光学精密机械研究所_中科院强激光材料重点实验室 |
| 作者单位 | 1.[Ling, Xiulan 2.Wang, Gao] North Univ China, Minist Educ, Key Lab Instrumentat Sci & Dynam Measurement, Taiyuan 030051, Peoples R China 3.[Ling, Xiulan 4.Wang, Gao] North Univ China, Key Lab Sci & Technol Elect Test & Measurement, Taiyuan 030051, Peoples R China 5.[Liu, Xiaofeng] Shanghai Inst Opt & Fine Mech, Key Lab Mat Sci & Technol High Power Lasers, Shanghai 201800, Peoples R China |
| 推荐引用方式 GB/T 7714 | Ling, Xiulan,Wang, Gao,Liu, Xiaofeng. Degradation mechanism of laser-induced damage of porous ZrO2/SiO2 high reflective films in vacuum[J]. optik,2015,126(19):2026. |
| APA | Ling, Xiulan,Wang, Gao,&Liu, Xiaofeng.(2015).Degradation mechanism of laser-induced damage of porous ZrO2/SiO2 high reflective films in vacuum.optik,126(19),2026. |
| MLA | Ling, Xiulan,et al."Degradation mechanism of laser-induced damage of porous ZrO2/SiO2 high reflective films in vacuum".optik 126.19(2015):2026. |
入库方式： OAI收割
来源：上海光学精密机械研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。