Structure and improved thermal stability of phenolic resin containing silicon and boron elements
文献类型：期刊论文
| 作者 | Li, Shan1,2; Chen, Fenghua1,2; Zhang, Boxing1,2; Luo, Zhenhua1,2; Li, Hao1; Zhao, Tong1,2 |
| 刊名 | POLYMER DEGRADATION AND STABILITY
 |
| 出版日期 | 2016-11-01 |
| 卷号 | 133页码:321-329 |
| 关键词 | Phenolic Boron Silicon Structure Thermal stability |
| 英文摘要 | Phenolic resin modified with silicon and boron (SNBA) was prepared by a simple two-step method: silane was firstly grafted onto phenolic resin, with silicon modified phenolic resin (SN) obtained; and then boric acid was introduced into SN. Boric acid, acting as a curing agent, catalyzed the self polymerization of the silane in SN, and induced phase separation in the cured SNBA systems. Thermal stability was evaluated by thermogravimetric analysis (TGA). In air, the maximum decomposition rate (Dmax) decreased about 2%/min and the residual weight at 900 degrees C (R-900) increased 16.7% after the introduction of boron and silicon. Oxyacetylene flame ablation also confirmed the improved ablative properties of the hybrids. The flame retardancy was studied by cone calorimeter. The total heat release (THR), the total smoke produce (TSP) and the rate of mass loss (RML) were decreased after the modification. The structure of the oxidized resin was characterized to study the mechanism of the improved thermal stability and flame retardancy. The oxide compounds of silicon and boron were formed during high temperature oxidation, which consumed some oxygen and hindered the permeation of heat and oxygen, protecting the matrix from thermal oxidation. (C) 2016 Elsevier Ltd. All rights reserved. |
| 收录类别 | SCI |
| 语种 | 英语 |
| 源URL | [http://ir.iccas.ac.cn/handle/121111/35496]  |
| 专题 | 化学研究所_高技术材料实验室 |
| 作者单位 | 1.Chinese Acad Sci, Inst Chem, Lab Adv Polymer Mat, Beijing 100790, Peoples R China 2.Univ Chinese Acad Sci, Beijing 100049, Peoples R China |
| 推荐引用方式 GB/T 7714 | Li, Shan,Chen, Fenghua,Zhang, Boxing,et al. Structure and improved thermal stability of phenolic resin containing silicon and boron elements[J]. POLYMER DEGRADATION AND STABILITY,2016,133:321-329. |
| APA | Li, Shan,Chen, Fenghua,Zhang, Boxing,Luo, Zhenhua,Li, Hao,&Zhao, Tong.(2016).Structure and improved thermal stability of phenolic resin containing silicon and boron elements.POLYMER DEGRADATION AND STABILITY,133,321-329. |
| MLA | Li, Shan,et al."Structure and improved thermal stability of phenolic resin containing silicon and boron elements".POLYMER DEGRADATION AND STABILITY 133(2016):321-329. |
入库方式： OAI收割
来源：化学研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。