The relationship between microstructure and flexural strength of pressureless liquid phase sintered SiC ceramics oxidized at elevated temperatures
文献类型:期刊论文
作者 | Liang, Hanqin1; Yao, Xiumin1; Huang, Zhengren1; Zeng, Yuping1; Su, Bizhe1,2,3 |
刊名 | CERAMICS INTERNATIONAL |
出版日期 | 2016-08-15 |
卷号 | 42期号:11页码:13256-13261 |
关键词 | SiC Liquid phase sintering Oxidation Microstructure |
英文摘要 | The oxidation behavior of pressureless liquid phase sintered SiC ceramics with Al2O3 and Y2O3 as sintering additives was investigated in the temperature range from 1000 degrees C to 1600 degrees C at the interval of 100 degrees C for 5 h. The relationship between residual flexural strength and microstructure was analyzed in detail. It was found that the SiC specimens suffered from mild oxidation below 1300 degrees C. The flexural strength of SiC specimens after oxidation at 1100 degrees C was the highest (90% of the original strength) due to the formation of dendritic grains, which filled pores and healed cracks. And the flexural strength was almost above 80% of the original flexural strength when the oxidation temperature was below 1300 degrees C. Meanwhile, the weight of specimens underwent steady increase. However, when the oxidation temperature was elevated to above 1400 degrees C, the specimens began to suffer from severe oxidation, which resulted in a lot of through pores and cracks on the surface, bringing about the sharp decrease of flexural strength to 30% of original strength when the oxidation temperature of 1600 degrees C was reached. And the weight of the specimens after huge increase began to show downtrend when the oxidation temperature was elevated to 1600 degrees C due to the spalling of oxidation products. (C) 2016 Elsevier Ltd and Techna Group S.r.l. All rights reserved. |
WOS标题词 | Science & Technology ; Technology |
类目[WOS] | Materials Science, Ceramics |
研究领域[WOS] | Materials Science |
关键词[WOS] | OXIDATION BEHAVIOR ; ADDITIVE CONTENT ; AIR ; RESISTANCE ; ER2O3 ; ALN |
收录类别 | SCI |
语种 | 英语 |
WOS记录号 | WOS:000378952100095 |
源URL | [http://ir.sic.ac.cn/handle/331005/22082] |
专题 | 上海硅酸盐研究所_结构陶瓷与复合材料工程研究中心_期刊论文 |
作者单位 | 1.Chinese Acad Sci, Shanghai Inst Ceram, State Key Lab High Performance Ceram & Superfine, Shanghai 200050, Peoples R China 2.ShanghaiTech Univ, Sch Phys Sci & Technol, 100 Haike Rd, Shanghai 201210, Peoples R China 3.Univ Chinese Acad Sci, 19 Yuquan Rd, Beijing 100039, Peoples R China |
推荐引用方式 GB/T 7714 | Liang, Hanqin,Yao, Xiumin,Huang, Zhengren,et al. The relationship between microstructure and flexural strength of pressureless liquid phase sintered SiC ceramics oxidized at elevated temperatures[J]. CERAMICS INTERNATIONAL,2016,42(11):13256-13261. |
APA | Liang, Hanqin,Yao, Xiumin,Huang, Zhengren,Zeng, Yuping,&Su, Bizhe.(2016).The relationship between microstructure and flexural strength of pressureless liquid phase sintered SiC ceramics oxidized at elevated temperatures.CERAMICS INTERNATIONAL,42(11),13256-13261. |
MLA | Liang, Hanqin,et al."The relationship between microstructure and flexural strength of pressureless liquid phase sintered SiC ceramics oxidized at elevated temperatures".CERAMICS INTERNATIONAL 42.11(2016):13256-13261. |
入库方式: OAI收割
来源:上海硅酸盐研究所
浏览0
下载0
收藏0
其他版本
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。