Searching for a fabrication route of efficient Cu2ZnSnS4 solar cells by post-sulfuration of co-sputtered Sn-enriched precursors
文献类型：期刊论文
| 作者 | Ye Feng; Bing Yu; Guanming Cheng; Tszki Lau; Zhaohui Li; Ling Yin; Qiuming Song; Chunlei Yang; Xudong Xiao |
| 刊名 | Journal of Materials Chemistry C
 |
| 出版日期 | 2015 |
| 英文摘要 | We have systematically investigated the Sn loss in the Cu2ZnSnS4 (CZTS) thin film formation process using a sputtering/sulfuration approach with highly Sn-enriched precursors. It was found that the remaining Sn content in the CZTS absorber is strongly dependent on the peak sulfuration temperature, H2S concentration in the sulfuration atmosphere, the temperature ramping rate, and the Zn content in the precursors. Since the Sn content could be controlled by the Sn loss during the thermal treatment process, the final composition of the CZTS thin films could be manipulated simply by tailoring the Cu/Zn ratio in the precursors. With such a route, highly efficient solar cells could be achieved from Sn-rich precursors |
| 收录类别 | SCI |
| 原文出处 | http://pubs.rsc.org/en/Content/ArticleLanding/2015/TC/C5TC02486B#!divAbstract |
| 语种 | 英语 |
| WOS记录号 | WOS:000367310200012 |
| 源URL | [http://ir.siat.ac.cn:8080/handle/172644/6581]  |
| 专题 | 深圳先进技术研究院_集成所 |
| 作者单位 | Journal of Materials Chemistry C |
| 推荐引用方式 GB/T 7714 | Ye Feng,Bing Yu,Guanming Cheng,et al. Searching for a fabrication route of efficient Cu2ZnSnS4 solar cells by post-sulfuration of co-sputtered Sn-enriched precursors[J]. Journal of Materials Chemistry C,2015. |
| APA | Ye Feng.,Bing Yu.,Guanming Cheng.,Tszki Lau.,Zhaohui Li.,...&Xudong Xiao.(2015).Searching for a fabrication route of efficient Cu2ZnSnS4 solar cells by post-sulfuration of co-sputtered Sn-enriched precursors.Journal of Materials Chemistry C. |
| MLA | Ye Feng,et al."Searching for a fabrication route of efficient Cu2ZnSnS4 solar cells by post-sulfuration of co-sputtered Sn-enriched precursors".Journal of Materials Chemistry C (2015). |
入库方式： OAI收割
来源：深圳先进技术研究院
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。