Tuneable cellular-structured 3D graphene aerogel and its effect on electromagnetic interference shielding performance and mechanical properties of epoxy composites
文献类型：期刊论文
| 作者 | Wan, Yan-Jun; Yu, Shu-Hui; Yang, Wen-Hu; Zhu, Peng-Li; Sun, Rong; Wong, Ching-Ping; Liao, Wei-Hsin |
| 刊名 | RSC ADVANCES
 |
| 出版日期 | 2016 |
| 英文摘要 | Microstructure design is a crucial factor in determining the performances of graphene/polymer composites. In this study, controllable cellular-structured graphene aerogel-epoxy composites (GA-EP) were fabricated by an infiltration method using porous GA as a framework; GA with different pore sizes and morphologies was tuned by employing precursor graphene oxide (GO) sheets with varied sizes. The structural morphology, electromagnetic interference shielding (EMI) performance and mechanical properties as well as the thermal stability of GA-EP composites were comprehensively and comparatively investigated. It was found that GA which originated from large-sized GO sheets after compounding with epoxy (LGA-EP) possesses superior EMI properties and compressive strength than those of GA assembled by small-sized GO sheets after integrating with epoxy (SGA-EP). LGA-EP with a thickness of 3 mm and loaded with similar to 1.0 wt% filler exhibits an EMI shielding effectiveness of around 30 dB in the measured frequency range of 10-20 GHz and compressive strength of 56.01 +/- 1.57 MPa. Both SGA-EP and LGA-EP exhibit excellent electrical conductivity, while the interconnected network with large graphene sheets in LGA-EP provides more effective and fast channels for electron transport than that of SGA-EP. The electrical conductivity of LGA-EP is up to 9.28 S m(-1) at only 1.0 wt% filler content. On the contrary, SGA-EP can obtain a higher storage modulus, glass transition temperature and thermal stability than those of LGA-EP. These results indicate that the macro-properties including EMI shielding, conductivity and mechanical properties of GA-polymer composites can be tailored by using precursor GO sheets with different sizes, and the GA-EP composites with excellent EMI performance have great potential applications in various fields such as electronics, automobiles and aircraft. |
| 收录类别 | SCI |
| 原文出处 | http://pubs.rsc.org/is/content/articlehtml/2016/ra/c6ra09459g |
| 语种 | 英语 |
| 源URL | [http://ir.siat.ac.cn:8080/handle/172644/9886]  |
| 专题 | 深圳先进技术研究院_集成所 |
| 作者单位 | RSC ADVANCES |
| 推荐引用方式 GB/T 7714 | Wan, Yan-Jun,Yu, Shu-Hui,Yang, Wen-Hu,et al. Tuneable cellular-structured 3D graphene aerogel and its effect on electromagnetic interference shielding performance and mechanical properties of epoxy composites[J]. RSC ADVANCES,2016. |
| APA | Wan, Yan-Jun.,Yu, Shu-Hui.,Yang, Wen-Hu.,Zhu, Peng-Li.,Sun, Rong.,...&Liao, Wei-Hsin.(2016).Tuneable cellular-structured 3D graphene aerogel and its effect on electromagnetic interference shielding performance and mechanical properties of epoxy composites.RSC ADVANCES. |
| MLA | Wan, Yan-Jun,et al."Tuneable cellular-structured 3D graphene aerogel and its effect on electromagnetic interference shielding performance and mechanical properties of epoxy composites".RSC ADVANCES (2016). |
入库方式： OAI收割
来源：深圳先进技术研究院
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。