Temperature characteristics of optical parameters of phthalocyanine LB films and spin-coated films
文献类型：期刊论文
| 作者 | Gu ZT ; Yin JL ; Liang PH ; Gan FX(干福熹) |
| 刊名 | opt. mater.
 |
| 出版日期 | 2005 |
| 卷号 | 27期号:10页码:1618 |
| 关键词 | phthalocyanine LB film spin-coating optical properties |
| ISSN号 | 0925-3467 |
| 中文摘要 | the lb films and spin-coated films of tetra-neopentoxy phthalocyanine zinc (tnppczn) were prepared and annealed at different temperatures. their refractive index (n) and extinction coefficient (k) were measured by p-polarized reflectance. the similar value of n and k, as well as similar changing tendency of it and k at varied annealing temperatures, was found between lb films and spin-coated films. in addition, the absorption curves of tnppczn lb films and spin-coated films in visible range at different annealing temperature were investigated. the results indicate that the changing tendency of the extinction coefficient of two kinds of tnppczn films obtained from two methods mentioned above were coincident. when the annealing temperature increased to 150 degrees c, the monomers of tnppczn films transformed to aggregates, n(f) and k(f) of the films increased. further, n(f) and k(f) decreased as aggregates changed back to monomers again at the annealing temperature of 300 degrees c. the experimental results coincide well with the theoretical analysis. (c) 2004 elsevier b.v. all rights reserved. |
| 收录类别 | EI |
| 语种 | 英语 |
| WOS记录号 | WOS:000231250700014 |
| 公开日期 | 2009-09-18 |
| 源URL | [http://ir.siom.ac.cn/handle/181231/2747]  |
| 专题 | 上海光学精密机械研究所_先进激光技术与应用系统实验室 |
| 推荐引用方式 GB/T 7714 | Gu ZT,Yin JL,Liang PH,et al. Temperature characteristics of optical parameters of phthalocyanine LB films and spin-coated films[J]. opt. mater.,2005,27(10):1618, 1622. |
| APA | Gu ZT,Yin JL,Liang PH,&干福熹.(2005).Temperature characteristics of optical parameters of phthalocyanine LB films and spin-coated films.opt. mater.,27(10),1618. |
| MLA | Gu ZT,et al."Temperature characteristics of optical parameters of phthalocyanine LB films and spin-coated films".opt. mater. 27.10(2005):1618. |
入库方式： OAI收割
来源：上海光学精密机械研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。