In vitro and in vivo studies on a Mg-Sr binary alloy system developed as a new kind of biodegradable metal
文献类型：期刊论文
| 作者 | X.N. Gu; X.H. Xie; N. Li; Y.F. Zheng; L. Qin |
| 刊名 | ACTA BIOMATERIALIA
 |
| 出版日期 | 2012 |
| 英文摘要 | Magnesium alloys have shown potential as biodegradable metallic materials for orthopedic applications due to their degradability, resemblance to cortical bone and biocompatible degradation/corrosion products. However, the fast corrosion rate and the potential toxicity of their alloying element limit the clinical application of Mg alloys. From the viewpoint of both metallurgy and biocompatibility, strontium (Sr) was selected to prepare hot rolled Mg-Sr binary alloys (with a Sr content ranging from 1 to 4 wt.%) in the present study. The optimal Sr content was screened with respect to the mechanical and corrosion properties of Mg-Sr binary alloys and the feasibility of the use of Mg-Sr alloys as orthopedic biodegradable metals was investigated by in vitro cell experiments and intramedullary implantation tests. The mechanical properties and corrosion rates of Mg-Sr alloys were dose dependent with respect to the added Sr content. The as-rolled Mg-2Sr alloy exhibited the highest strength and slowest corrosion rate, suggesting that the optimal Sr content was 2 wt.%. The as-rolled Mg-2Sr alloy showed Grade I cytotoxicity and induced higher alkaline phosphatase activity than the other alloys. During the 4 weeks implantation period we saw gradual degradation of the as-rolled Mg-2Sr alloy within a bone tunnel. Micro-computer tomography and histological analysis showed an enhanced mineral density and thicker cortical bone around the experimental implants. Higher levels of Sr were observed in newly formed pen-implant bone compared with the control. In summary, this study shows that the optimal content of added Sr is 2 wt.% for binary Mg-Sr alloys in the rolled state and that the as-rolled Mg-2Sr alloy in vivo produces an acceptable host response. |
| 收录类别 | SCI |
| 原文出处 | http://ac.els-cdn.com/S1742706112000827/1-s2.0-S1742706112000827-main.pdf?_tid=242e1378-0937-11e5-b113-00000aab0f6b&acdnat=1433256994_e8ced8f82159ede536dd1447af6035c4 |
| 语种 | 英语 |
| 源URL | [http://ir.siat.ac.cn:8080/handle/172644/4018]  |
| 专题 | 深圳先进技术研究院_医工所 |
| 作者单位 | ACTA BIOMATERIALIA |
| 推荐引用方式 GB/T 7714 | X.N. Gu,X.H. Xie,N. Li,et al. In vitro and in vivo studies on a Mg-Sr binary alloy system developed as a new kind of biodegradable metal[J]. ACTA BIOMATERIALIA,2012. |
| APA | X.N. Gu,X.H. Xie,N. Li,Y.F. Zheng,&L. Qin.(2012).In vitro and in vivo studies on a Mg-Sr binary alloy system developed as a new kind of biodegradable metal.ACTA BIOMATERIALIA. |
| MLA | X.N. Gu,et al."In vitro and in vivo studies on a Mg-Sr binary alloy system developed as a new kind of biodegradable metal".ACTA BIOMATERIALIA (2012). |
入库方式： OAI收割
来源：深圳先进技术研究院
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。