Strontium exerts dual effects on calcium phosphate cement: Accelerating the degradation and enhancing the osteoconductivity both in vitro and in vivo
文献类型：期刊论文
| 作者 | Kuang GuanMing; Yau W. P.; Wu Jun; Yeung Kelvin W. K.; Pan Haobo; Lam W. M.; Lu W. W.; Chiu K. Y. |
| 刊名 | JOURNAL OF BIOMEDICAL MATERIALS RESEARCH PART A
 |
| 出版日期 | 2015 |
| 英文摘要 | Calcium phosphate cements (CPCs) have long been used as osteoconductive bone substitutes in the treatment of bone defects. However, the degradation rate of CPC is typically too slow to match the new bone growth rate. It is known that strontium increases the solubility of hydroxyapatite as well as exerts both anabolic and anticatabolic effects on bone. Therefore, we hypothesized that the incorporation of strontium would accelerate the degradation rate and enhance the osteoconductivity of CPC. In this study, Three groups, CPC (0% Sr-CPC), 5% Sr-CPC, and 10% Sr-CPC, were prepared, with the total molar ratio for Sr/(Sr+Ca) in the cement powder phase being 0, 5, and 10%, respectively. In the immersion test, less residual weight was observed in both 5% Sr-CPC and 10% Sr-CPC groups than CPC group. In addition, a higher osteoblastic cell proliferation rate and alkaline phosphatase activity were obtained in the strontium groups. In a rat femur bone defect model comparing CPC with 10% Sr-CPC, at 2 weeks postoperation, early endochondral ossification was found in the 10% Sr-CPC group, whereas only fibrous tissue was observed in control group; at 4-16 weeks postoperation, progressive osteoconduction toward the cement was observed in both groups. At 32 weeks, a higher peri-cement bone area and reduced cement area were noted in the 10% Sr-CPC group. In conclusion, in the 10% Sr-CPC group, strontium exerts dual effects on CPC: accelerating degradation rate and enhancing osteoconductivity, as shown here both in vitro and in vivo. (c) 2014 Wiley Periodicals, Inc. J Biomed Mater Res Part A: 103A: 1613-1621, 2015 |
| 收录类别 | SCI |
| 原文出处 | http://www.ncbi.nlm.nih.gov/pubmed/25087971 |
| 语种 | 英语 |
| 源URL | [http://ir.siat.ac.cn:8080/handle/172644/7384]  |
| 专题 | 深圳先进技术研究院_医药所 |
| 作者单位 | JOURNAL OF BIOMEDICAL MATERIALS RESEARCH PART A |
| 推荐引用方式 GB/T 7714 | Kuang GuanMing,Yau W. P.,Wu Jun,et al. Strontium exerts dual effects on calcium phosphate cement: Accelerating the degradation and enhancing the osteoconductivity both in vitro and in vivo[J]. JOURNAL OF BIOMEDICAL MATERIALS RESEARCH PART A,2015. |
| APA | Kuang GuanMing.,Yau W. P..,Wu Jun.,Yeung Kelvin W. K..,Pan Haobo.,...&Chiu K. Y..(2015).Strontium exerts dual effects on calcium phosphate cement: Accelerating the degradation and enhancing the osteoconductivity both in vitro and in vivo.JOURNAL OF BIOMEDICAL MATERIALS RESEARCH PART A. |
| MLA | Kuang GuanMing,et al."Strontium exerts dual effects on calcium phosphate cement: Accelerating the degradation and enhancing the osteoconductivity both in vitro and in vivo".JOURNAL OF BIOMEDICAL MATERIALS RESEARCH PART A (2015). |
入库方式： OAI收割
来源：深圳先进技术研究院
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。