Effect of HfC and SiC on microstructure and mechanical properties of HfB2-based ceramics
文献类型：期刊论文
| 作者 | Yuan, Ye1,2; Liu, Ji-Xuan1; Zhang, Guo-Jun1 |
| 刊名 | CERAMICS INTERNATIONAL
 |
| 出版日期 | 2016-05-01 |
| 卷号 | 42期号:6页码:7861-7867 |
| 关键词 | Hot pressing Composites Mechanical properties Structural applications |
| 英文摘要 | SiC and HfC were used to tailor microstructures and improve properties of hot pressed HfB2-based ceramics. SiC and HfC particle, as the second phase, could hinder grain growth of HfB2. Compared with HfC, SiC grains grew slower, which was more effective to hinder grain growth of HfB2. The ternary ceramics HfB2-20vol%HfC-20vol%SiC had the finest microstructure, indicating the effect of SiC and HfC on grain growth. Several SiC clusters were found on related fracture surfaces. Large SiC clusters can cause high levels of residual stress and stress concentration, which are harmful to mechanical properties of boride-SiC ceramics. The predominant fracture mode of HfB2-20vol%SiC was transgranular, however, in HfB2-10vol%HfC-10vol%SiC and HfB2-20vol%HfC-20vol%SiC ceramics, the dominating fracture mode shift from transgranular to intergranular. With the incorporation of HfC, the fracture toughness of HH10S10 and HH2OS20 increased to 4.34 MPa m(1/2) and 5.05 MPa m(1/2), which were 17.3% and 26.7% higher than HS2O (3.72 MPa m(1/2)), respectively. The flexural strengths of HfB2 HfC SiC ceramics were improved to similar to 750 MPa, which were about 1.3 times higher than that of HfB2-20SiC. (C) 2016 Elsevier Ltd and Techna Group S.r.l. All rights reserved. |
| WOS标题词 | Science & Technology ; Technology |
| 类目[WOS] | Materials Science, Ceramics |
| 研究领域[WOS] | Materials Science |
| 关键词[WOS] | HIGH-TEMPERATURE CERAMICS ; COMPOSITES ; HAFNIUM ; REDUCTION ; EVOLUTION ; POWDER |
| 收录类别 | SCI |
| 语种 | 英语 |
| WOS记录号 | WOS:000372676000162 |
| 源URL | [http://ir.sic.ac.cn/handle/331005/23018]  |
| 专题 | 上海硅酸盐研究所_高性能陶瓷和超微结构国家重点实验室_期刊论文 |
| 作者单位 | 1.Shanghai Inst Ceram, State Key Lab High Peiformance Ceram & Superfine, Shanghai 200050, Peoples R China 2.Univ Chinese Acad Sci, Beijing 100049, Peoples R China |
| 推荐引用方式 GB/T 7714 | Yuan, Ye,Liu, Ji-Xuan,Zhang, Guo-Jun. Effect of HfC and SiC on microstructure and mechanical properties of HfB2-based ceramics[J]. CERAMICS INTERNATIONAL,2016,42(6):7861-7867. |
| APA | Yuan, Ye,Liu, Ji-Xuan,&Zhang, Guo-Jun.(2016).Effect of HfC and SiC on microstructure and mechanical properties of HfB2-based ceramics.CERAMICS INTERNATIONAL,42(6),7861-7867. |
| MLA | Yuan, Ye,et al."Effect of HfC and SiC on microstructure and mechanical properties of HfB2-based ceramics".CERAMICS INTERNATIONAL 42.6(2016):7861-7867. |
入库方式： OAI收割
来源：上海硅酸盐研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。