Thermal shock behavior of pressureless liquid phase sintered SiC ceramics
文献类型：期刊论文
| 作者 | Liang, Hanqin; Yao, Xiumin; Huang, Zhengren; Zeng, Yuping; Su, Bizhe |
| 刊名 | CERAMICS INTERNATIONAL
 |
| 出版日期 | 2016-05-15 |
| 卷号 | 42期号:7页码:8677-8683 |
| 关键词 | D. SiC Liquid phase sintering Oxidation Thermal shock |
| 英文摘要 | The thermal shock behavior of pressureless liquid phase sintered (PLPS) SiC ceramics with Al2O3 and Y2O3 as sintering additives was investigated by using water quenching method with the temperature difference from 200 degrees C to 1400 degrees C. It was found the residual flexural strength of PLPS SiC dropped quickly to about 100 MPa when the temperature difference reached 600 degrees C due to the cracks induced by thermal stress. The residual flexural strength of the PLPS SiC increased when the temperature difference reached 1300 degrees C and 1400 degrees C due to the formation of SiO2 oxide layers, which acted as thermal barriers to reduce the thermal stress on the surface of the SiC ceramics. However, comparing the microstructure of specimens quenched at Delta T=1300 degrees C and 1400 degrees C, the slight decrease of residual flexural strength at Delta T= 1400 degrees C was due to the formation of large amount of through pores in the oxide layer, which was speculated to be the strength-limiting flaw above 1300 degrees C. (C) 2016 Elsevier Ltd and Techna Group S.r.l. All rights reserved. |
| WOS标题词 | Science & Technology ; Technology |
| 类目[WOS] | Materials Science, Ceramics |
| 研究领域[WOS] | Materials Science |
| 关键词[WOS] | MECHANICAL-PROPERTIES ; OXIDATION BEHAVIOR ; RESISTANCE ; COMPOSITES ; MICROSTRUCTURE ; SPS ; DENSIFICATION ; ATMOSPHERE ; ADDITIVES ; TOUGHNESS |
| 收录类别 | SCI |
| 语种 | 英语 |
| WOS记录号 | WOS:000374075300105 |
| 源URL | [http://ir.sic.ac.cn/handle/331005/23036]  |
| 专题 | 上海硅酸盐研究所_结构陶瓷与复合材料工程研究中心_期刊论文 |
| 作者单位 | Chinese Acad Sci, Shanghai Inst Ceram, State Key Lab High Performance Ceram & Superfine, Shanghai 200050, Peoples R China |
| 推荐引用方式 GB/T 7714 | Liang, Hanqin,Yao, Xiumin,Huang, Zhengren,et al. Thermal shock behavior of pressureless liquid phase sintered SiC ceramics[J]. CERAMICS INTERNATIONAL,2016,42(7):8677-8683. |
| APA | Liang, Hanqin,Yao, Xiumin,Huang, Zhengren,Zeng, Yuping,&Su, Bizhe.(2016).Thermal shock behavior of pressureless liquid phase sintered SiC ceramics.CERAMICS INTERNATIONAL,42(7),8677-8683. |
| MLA | Liang, Hanqin,et al."Thermal shock behavior of pressureless liquid phase sintered SiC ceramics".CERAMICS INTERNATIONAL 42.7(2016):8677-8683. |
入库方式： OAI收割
来源：上海硅酸盐研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。