Reaction-Bonded B4C with High Hardness
文献类型：期刊论文
| 作者 | Li, Xiaoguang; Jiang, Dongliang; Zhang, Jingxian; Zhu, Yunzhou; Chen, Zhongming; Huang, Zhengren |
| 刊名 | INTERNATIONAL JOURNAL OF APPLIED CERAMIC TECHNOLOGY
 |
| 出版日期 | 2016-05-01 |
| 卷号 | 13期号:3页码:584-592 |
| 英文摘要 | Reaction-bonded B4C (RBBC) was fabricated through molten Si infiltrating porous B4C preforms. A preform with a 75% relative green density was obtained by mixing two different sized B4C powders. Carbon black added to the preform slightly reduces average pore size, but increases porosity. RBBC ceramics showed a dense and homogeneous microstructure. Vickers hardness was about 15 GPa for RBBC fabricated from a single type of B4C powder and could reach 22-23 GPa for the carbon-added samples after infiltration. Morphological evolution and the influence of the microstructure on the Vickers hardness were investigated and discussed. |
| WOS标题词 | Science & Technology ; Technology |
| 类目[WOS] | Materials Science, Ceramics |
| 研究领域[WOS] | Materials Science |
| 关键词[WOS] | MECHANICAL-PROPERTIES ; BORON-CARBIDE ; SILICON-CARBIDE ; MICROSTRUCTURE ; COMPOSITES ; EVOLUTION ; PACKING |
| 收录类别 | SCI |
| 语种 | 英语 |
| WOS记录号 | WOS:000375112400020 |
| 源URL | [http://ir.sic.ac.cn/handle/331005/23115]  |
| 专题 | 上海硅酸盐研究所_结构陶瓷与复合材料工程研究中心_期刊论文 |
| 作者单位 | Chinese Acad Sci, Shanghai Inst Ceram, State Key Lab High Performance Ceram & Superfine, Shanghai 200050, Peoples R China |
| 推荐引用方式 GB/T 7714 | Li, Xiaoguang,Jiang, Dongliang,Zhang, Jingxian,et al. Reaction-Bonded B4C with High Hardness[J]. INTERNATIONAL JOURNAL OF APPLIED CERAMIC TECHNOLOGY,2016,13(3):584-592. |
| APA | Li, Xiaoguang,Jiang, Dongliang,Zhang, Jingxian,Zhu, Yunzhou,Chen, Zhongming,&Huang, Zhengren.(2016).Reaction-Bonded B4C with High Hardness.INTERNATIONAL JOURNAL OF APPLIED CERAMIC TECHNOLOGY,13(3),584-592. |
| MLA | Li, Xiaoguang,et al."Reaction-Bonded B4C with High Hardness".INTERNATIONAL JOURNAL OF APPLIED CERAMIC TECHNOLOGY 13.3(2016):584-592. |
入库方式： OAI收割
来源：上海硅酸盐研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。