The improved mechanical properties of beta-CaSiO3 bioceramics with Si3N4 addition
文献类型：期刊论文
| 作者 | Pan, Ying1,2; Zuo, Kaihui1; Yao, Dongxu1; Yin, Jinwei1; Xie, Yunchuan1,2; Xia, Yongfeng1; Liang, Hanqin1; Zeng, Yuping1 |
| 刊名 | JOURNAL OF THE MECHANICAL BEHAVIOR OF BIOMEDICAL MATERIALS
 |
| 出版日期 | 2016-03-01 |
| 卷号 | 55页码:120-126 |
| 关键词 | beta-CaSiO3 Si3N4 Oxidation Mechanical properties |
| 英文摘要 | The motivation of this study is to investigate the effect of Si3N4 addition on the sinterability of beta-CaSiO3 ceramics. beta-CaSiO3 ceramics with different content of Si3N4 were prepared at the sintering temperature ranging from 1000 degrees C to 1150 degrees C. The results showed that Si3N4 can be successfully used as sintering additive by being oxidized to form SiO2. The beta-CaSiO3 ceramics with 3 wt% Si3N4 sintered at 1100 degrees C revealed flexural strength, hardness and fracture toughness of 157.2 MPa, 4.4 GPa and 2.3 MPa m(1/2) respectively, which was much higher than that of pure beta-CaSiO3 ceramics (41.1 MPa, 1.0 GPa, 1.1 MPa m(1/2)). XRD analysis and SEM observation indicated that the main phase maintained to be beta-phase after sintering. (C) 2015 Elsevier Ltd. All rights reserved. |
| WOS标题词 | Science & Technology ; Technology |
| 类目[WOS] | Engineering, Biomedical ; Materials Science, Biomaterials |
| 研究领域[WOS] | Engineering ; Materials Science |
| 关键词[WOS] | BONDED SILICON-NITRIDE ; CALCIUM SILICATE ; IN-VITRO ; CERAMICS ; STRENGTH ; POROSITY ; DENSE ; WOLLASTONITE ; BIOACTIVITY ; OXIDATION |
| 收录类别 | SCI |
| 语种 | 英语 |
| WOS记录号 | WOS:000370886600011 |
| 源URL | [http://ir.sic.ac.cn/handle/331005/23214]  |
| 专题 | 上海硅酸盐研究所_结构陶瓷与复合材料工程研究中心_期刊论文 |
| 作者单位 | 1.Chinese Acad Sci, Shanghai Inst Ceram, State Key Lab High Performance Ceram & Superfine, Shanghai 200050, Peoples R China 2.Chinese Acad Sci, Grad Sch, Beijing 100049, Peoples R China |
| 推荐引用方式 GB/T 7714 | Pan, Ying,Zuo, Kaihui,Yao, Dongxu,et al. The improved mechanical properties of beta-CaSiO3 bioceramics with Si3N4 addition[J]. JOURNAL OF THE MECHANICAL BEHAVIOR OF BIOMEDICAL MATERIALS,2016,55:120-126. |
| APA | Pan, Ying.,Zuo, Kaihui.,Yao, Dongxu.,Yin, Jinwei.,Xie, Yunchuan.,...&Zeng, Yuping.(2016).The improved mechanical properties of beta-CaSiO3 bioceramics with Si3N4 addition.JOURNAL OF THE MECHANICAL BEHAVIOR OF BIOMEDICAL MATERIALS,55,120-126. |
| MLA | Pan, Ying,et al."The improved mechanical properties of beta-CaSiO3 bioceramics with Si3N4 addition".JOURNAL OF THE MECHANICAL BEHAVIOR OF BIOMEDICAL MATERIALS 55(2016):120-126. |
入库方式： OAI收割
来源：上海硅酸盐研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。