Comparative study on fiber laser welding of GH3535 superalloy in continuous and pulsed waves
文献类型：期刊论文
| 作者 | Jiang, ZG; Tao, W; Yu, K; Tan, CW; Chen, YB; Li, LQ; Li, ZJ |
| 刊名 | MATERIALS & DESIGN
 |
| 出版日期 | 2016 |
| 卷号 | 110页码:728-739 |
| 关键词 | Laser welding GH3535 superalloy Pulsed wave Microstructure Mechanical properties |
| ISSN号 | 0264-1275 |
| 通讯作者 | Tao, W ; Tan, CW (reprint author), Harbin Inst Technol, State Key Lab Adv Welding & Joining, Harbin 150001, Peoples R China. |
| 英文摘要 | GH3535 superalloy is the candidate structural material for the next-generation nuclear reactors and its related welding problem is inevitable and needs to be solved. In this work, fiber laser welding of 4-mm-thick GH3535 superalloy in continuous wave (CW) and pulsed wave (PW) was comparatively investigated. The weld appearances, dynamic behavior of weld pool, microstructure and mechanical properties in both cases were studied. The results indicated that larger porosities were present in the bottom of the CW joint while few porosities appeared in the PW joint. The laser weld zone of both CW and PW joints was still composed of gamma-Ni matrix and M6C carbides. Grain size of PW joint was smaller than that of CW joint. More precipitated particles were found in the PW joint. The presence of porosity in the CW joint reduced mechanical properties greatly. The tensile strength decreased to 85% of that of base metal at room temperature, and 82.3% at high temperature while the PW joint strength could reach 97.6% and 95.7% at room and high temperature, respectively. The fracture surface of CW joint had a flat pattern and porosities, while PW joint exhibited dimples on the fracture surface both at room and high temperature. (C) 2016 Published by Elsevier Ltd. |
| 收录类别 | SCI |
| 语种 | 英语 |
| WOS记录号 | WOS:000385600800078 |
| 源URL | [http://ir.sinap.ac.cn/handle/331007/26453]  |
| 专题 | 上海应用物理研究所_中科院上海应用物理研究所2011-2017年 |
| 推荐引用方式 GB/T 7714 | Jiang, ZG,Tao, W,Yu, K,et al. Comparative study on fiber laser welding of GH3535 superalloy in continuous and pulsed waves[J]. MATERIALS & DESIGN,2016,110:728-739. |
| APA | Jiang, ZG.,Tao, W.,Yu, K.,Tan, CW.,Chen, YB.,...&Li, ZJ.(2016).Comparative study on fiber laser welding of GH3535 superalloy in continuous and pulsed waves.MATERIALS & DESIGN,110,728-739. |
| MLA | Jiang, ZG,et al."Comparative study on fiber laser welding of GH3535 superalloy in continuous and pulsed waves".MATERIALS & DESIGN 110(2016):728-739. |
入库方式： OAI收割
来源：上海应用物理研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。