Effect of Solution Heat Treatment on Microstructure and Properties of GH3535 Superalloy
文献类型：期刊论文
| 作者 | Zhang, WZ; Xu, ZF; Jiang, L |
| 刊名 | RARE METAL MATERIALS AND ENGINEERING
 |
| 出版日期 | 2016 |
| 卷号 | 45期号:6页码:1583-1587 |
| ISSN号 | 1002-185X |
| 关键词 | GH3535 superalloy solution heat treatment tensile properties carbides |
| 通讯作者 | Jiang, L (reprint author), Chinese Acad Sci, Thorium Molten Salts Reactor Ctr, Shanghai 201800, Peoples R China. |
| 英文摘要 | The effect of solution heat treatment on the microstructure and properties of hot-rolled GH3535 superalloy has been investigated by scanning electron microscope (SEM), electron back scattered diffraction (EBSD) and tensile tests. Results show that significant grain growth and carbide dissolution occur after solution treatment at 1177 degrees C for 20 min. With the rise of the solution temperature up to 1220 degrees C and 1260 degrees C, the grain size grows abnormally and the amounts of M6C carbides decrease significantly. Tensile tests indicate that higher solution temperature and longer solution time decrease the ultimate tensile strength and improve the elongation. The grain growth and carbide dissolution are responsible for the evolution of tensile properties in GH3535 superalloy after different solution heat treatments. |
| 收录类别 | SCI |
| 语种 | 中文 |
| WOS记录号 | WOS:000379195400040 |
| 源URL | [http://ir.sinap.ac.cn/handle/331007/26488]  |
| 专题 | 上海应用物理研究所_中科院上海应用物理研究所2011-2017年 |
| 推荐引用方式 GB/T 7714 | Zhang, WZ,Xu, ZF,Jiang, L. Effect of Solution Heat Treatment on Microstructure and Properties of GH3535 Superalloy[J]. RARE METAL MATERIALS AND ENGINEERING,2016,45(6):1583-1587. |
| APA | Zhang, WZ,Xu, ZF,&Jiang, L.(2016).Effect of Solution Heat Treatment on Microstructure and Properties of GH3535 Superalloy.RARE METAL MATERIALS AND ENGINEERING,45(6),1583-1587. |
| MLA | Zhang, WZ,et al."Effect of Solution Heat Treatment on Microstructure and Properties of GH3535 Superalloy".RARE METAL MATERIALS AND ENGINEERING 45.6(2016):1583-1587. |
入库方式： OAI收割
来源：上海应用物理研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。