M2C and M6C carbide precipitation in Ni-Mo-Cr based superalloys containing silicon
文献类型：期刊论文
| 作者 | Jiang, L; Zhang, WZ; Xu, ZF; Huang, HF; Ye, XX; Leng, B; Yan, L; Li, ZJ; Zhou, XT |
| 刊名 | MATERIALS & DESIGN
 |
| 出版日期 | 2016 |
| 卷号 | 112页码:300-308 |
| 关键词 | Si content Grain boundary carbides Electron backscatter diffraction Ni-Mo-Cr |
| ISSN号 | 0264-1275 |
| 通讯作者 | Yan, L ; Li, ZJ (reprint author), Chinese Acad Sci, Shanghai Inst Appl Phys, Thorium Molten Salts Reactor Ctr, Shanghai 201800, Peoples R China. |
| 英文摘要 | The effect of silicon additions on the primary carbides and second grain boundary carbides has been investigated in as-cast and wrought Ni-Mo-Cr based alloys, respectively. With the increase of Si content in the as-cast alloys, the lamellar M2C eutectic carbides at grain boundaries were replaced by skeleton-shape M6C eutectic carbides in interdendritic regions. The wrought alloys with different Si contents were thermal exposed at 750 degrees C for 1, 500 and 2000 h, respectively. It can be observed that the initial M2C carbides formed at grain boundaries were replaced by M6C carbides in the low-Si alloys (0.051 and 0.188 wt.%) with the increase of exposure time. Only M6C carbides precipitated at grain boundaries in the alloy with 0.562wt.% Si, which coarsened during the thermal exposure. Similar trends also existed in the high-Si alloy except an abnormal formation of M2C carbides after 2000 h' exposure. The effect of Si additions on the types of carbides was attributed to competitive nucleation between M2C carbides and M6C carbides based on classical nucleation theory. (C) 2016 Elsevier Ltd. All rights reserved. |
| 收录类别 | SCI |
| 语种 | 英语 |
| WOS记录号 | WOS:000387279700033 |
| 源URL | [http://ir.sinap.ac.cn/handle/331007/26566]  |
| 专题 | 上海应用物理研究所_中科院上海应用物理研究所2011-2017年 |
| 推荐引用方式 GB/T 7714 | Jiang, L,Zhang, WZ,Xu, ZF,et al. M2C and M6C carbide precipitation in Ni-Mo-Cr based superalloys containing silicon[J]. MATERIALS & DESIGN,2016,112:300-308. |
| APA | Jiang, L.,Zhang, WZ.,Xu, ZF.,Huang, HF.,Ye, XX.,...&Zhou, XT.(2016).M2C and M6C carbide precipitation in Ni-Mo-Cr based superalloys containing silicon.MATERIALS & DESIGN,112,300-308. |
| MLA | Jiang, L,et al."M2C and M6C carbide precipitation in Ni-Mo-Cr based superalloys containing silicon".MATERIALS & DESIGN 112(2016):300-308. |
入库方式： OAI收割
来源：上海应用物理研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。