Performance and structure changes of the aromatic co-polysulfonamide fibers during thermal-oxidative aging process
文献类型：期刊论文
| 作者 | Yu, JC; Chen, K; Li, XY; Tian, F; Chen, SH; Zhang, YM; Wang, HP |
| 刊名 | JOURNAL OF APPLIED POLYMER SCIENCE
 |
| 出版日期 | 2016 |
| 卷号 | 133期号:41页码:- |
| 关键词 | ageing fibers structure-property relations thermal properties |
| ISSN号 | 0021-8995 |
| 通讯作者 | Zhang, YM (reprint author), Donghua Univ, Coll Mat Sci & Engn, State Key Lab Modificat Chem Fibers & Polymer Mat, Shanghai 201620, Peoples R China. |
| 英文摘要 | The changes in performance during thermal-oxidative aging process of the aromatic co-polysulfonamide (co-PSA) fibers over a broad temperature range from 250 degrees C to 320 degrees C have been investigated. In addition, the mechanism of thermal-oxidative aging process has been studied by using structural information obtained from the fibers at varying length scales. The results showed that a significant reduction in tensile strength was observed compared with that of initial modulus during aging process. Macroscopically, thermal-oxidative aging mainly causes color changes of fibers and thermally induced macro defects begin to appear only at 320 degrees C for 100 h. On a micro level, the crystal structure of fibers remained stable and did not show significant changes expect that aging at 320 degrees C. In addition, thermo-degradation as well as crosslinking has been observed primarily in amorphous region. With the increase of temperature and time duration, the crosslinking became more dominant and crosslinking density increases. Correspondingly, the fibril length decreases due to degradation and then increases due to the formation of crosslinked structures within the fibers. The results suggest that molecular degradation is the main cause of strength loss and the formation of crosslinking structure within the fibers contributes to the retention of modulus and improvement of creep resistance. (C) 2016 Wiley Periodicals, Inc. |
| 收录类别 | SCI |
| 语种 | 英语 |
| WOS记录号 | WOS:000380728200013 |
| 源URL | [http://ir.sinap.ac.cn/handle/331007/26595]  |
| 专题 | 上海应用物理研究所_中科院上海应用物理研究所2011-2017年 |
| 推荐引用方式 GB/T 7714 | Yu, JC,Chen, K,Li, XY,et al. Performance and structure changes of the aromatic co-polysulfonamide fibers during thermal-oxidative aging process[J]. JOURNAL OF APPLIED POLYMER SCIENCE,2016,133(41):-. |
| APA | Yu, JC.,Chen, K.,Li, XY.,Tian, F.,Chen, SH.,...&Wang, HP.(2016).Performance and structure changes of the aromatic co-polysulfonamide fibers during thermal-oxidative aging process.JOURNAL OF APPLIED POLYMER SCIENCE,133(41),-. |
| MLA | Yu, JC,et al."Performance and structure changes of the aromatic co-polysulfonamide fibers during thermal-oxidative aging process".JOURNAL OF APPLIED POLYMER SCIENCE 133.41(2016):-. |
入库方式： OAI收割
来源：上海应用物理研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。